| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/PET Polyester Blend , Polyester, TP , Polyethylene Terephthalate (PET) |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DSM Stapron® E EM 605 Polycarbonate/PET Blend (European Grade)
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by DSM.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.21 g/cc | 0.0437 lb/in³ | ISO 1183 |
| Water Absorption | 0.35 % | 0.35 % | Sim. to ISO 62 |
| Melt Flow | 8.47 g/10 min @Load 1.20 kg, Temperature 280 °C |
8.47 g/10 min @Load 2.65 lb, Temperature 536 °F |
Calculated from Volume Flow Rate of 7 cm<sup>3</sup>/10min.; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | ISO 527-1/-2 |
| Elongation at Break | >= 50 % | >= 50 % | ISO 527-1/-2 |
| Elongation at Yield | 6.0 % | 6.0 % | ISO 527-1/-2 |
| Tensile Modulus | 2.20 GPa | 319 ksi | ISO 527-1/-2 |
| Flexural Strength | 80.0 MPa | 11600 psi | ISO 178 |
| Flexural Modulus | 2.20 GPa | 319 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 40.0 kJ/m² @Temperature -40.0 °C |
19.0 ft-lb/in² @Temperature -40.0 °F |
ISO 180/4A |
| 60.0 kJ/m² @Temperature -20.0 °C |
28.6 ft-lb/in² @Temperature -4.00 °F |
ISO 180/4A | |
| 70.0 kJ/m² @Temperature 23.0 °C |
33.3 ft-lb/in² @Temperature 73.4 °F |
ISO 180/4A | |
| Charpy Impact Unnotched | NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
ISO 179/1eU |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 2.50 J/cm² @Temperature -30.0 °C |
11.9 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 5.50 J/cm² @Temperature 23.0 °C |
26.2 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 80.0 µm/m-°C @Temperature 20.0 °C |
44.4 µin/in-°F @Temperature 68.0 °F |
ISO 11359-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 120 °C | 248 °F | ISO 75-1/-2 |
| Vicat Softening Point | 125 °C | 257 °F | 50°C/h 50N; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
IEC 60695-11-10 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Heat stabilized or stable to heat | Yes | |
| High impact or impact modified | Yes | |
| Injection molding | Yes | |
| Without Fillers | Yes |
Users viewing this material also viewed the following:
- Nilit FRIANYL B63 L-HS-GV15 Nylon 6 for injection molding, 15% glass fiber reinforced
- Huntsman IROGRAN® A 70 H 4673 M Polyester-Based TPU-Injection Molding Grade
- Materion Beryllium Copper Alloy 25 Plate & Rolled Bar; HT (TH04) Temper; over 9.5 to 25 mm Thickness (UNS C17200)
- LG Chemical LUPOY GP1000MU PC, Transparent
- Shin-Etsu Silicones 543 Fluid
- A. Schulman POLYBATCH™ Bright White P80514PF Concentrate Based In Polypropylene
- Arlon 51044R020 0.020" Semi-Cured Silicone Rubber with Fiberglass Substrate
- C.O.I.M. LARIPUR® LPR8520 Standard Adipate Ester Polyurethane
- Axiall 15881 Wire & Cable Flexible PVC
Copyright © lookpolymers.com All Rights Reserved