Armstrong A-10-T Epoxy Adhesive

Category Polymer , Adhesive , Thermoset , Epoxy , Epoxy Adhesive
Manufacturer Armstrong Epoxy Adhesives; Resin Technology Group
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Armstrong A-10-T Epoxy Adhesive.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Clear, thixotropic, 5-minute cure general-purpose epoxy adhesive. Provides rapid high strength bonds to many substrates. Supplied in 1:1 ratio dispense kits for easy application.Information provided by Ellsworth Adhesives.
Mechanical Properties Metric English Comments
Hardness, Shore D 74
74
Tensile Strength, Ultimate 38.6 MPa
5600 psi
after optimum cure
Elongation at Break 4.0 %
4.0 %
Adhesive Bond Strength 32.8 MPa
4750 psi
Steel-Steel; after optimum cure
13.4 MPa

@Temperature -54.4 °C
 1940 psi

@Temperature -66.0 °F
 Aluminum-Aluminum tensile shear
14.5 MPa

@Temperature 82.2 °C
 2100 psi

@Temperature 180 °F
 Aluminum-Aluminum tensile shear
25.2 MPa

@Temperature 25.0 °C
 3650 psi

@Temperature 77.0 °F
 Aluminum-Aluminum tensile shear
Thermal Properties Metric English Comments
CTE, linear 72.0 µm/m-°C

@Temperature 20.0 °C
 40.0 µin/in-°F

@Temperature 68.0 °F
Glass Transition Temp, Tg 63.0 °C
145 °F
Processing Properties Metric English Comments
Processing Temperature 22.2 °C
72.0 °F
73.9 °C
165 °F
Optimum cure is 20 min. @ 165°F
Pot Life <= 5.00 min

@Temperature 25.0 °C
 <= 5.00 min

@Temperature 77.0 °F
 100 g
Descriptive Properties Value Comments
Color Clear Straw
Mix Ratio 100/100
By Weight