DSM Akulon® XP36-E1 PA6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Film Grade |
| Manufacturer | DSM Engineering Plastics |
| Trade Name | Akulon® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DSM Akulon® XP36-E1 PA6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Film Extrusion, Medium Viscosity, Nucleated, Lubricated
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ISO 1183 |
| Water Vapor Transmission | 35.0 g/m²/day @Temperature 23.0 °C |
2.25 g/100 in²/day @Temperature 73.4 °F |
at 85% r.h., Film; DIS 15106-1/-3 |
| Oxygen Transmission | 1.05 cc-mm/m²-24hr-atm @Temperature 23.0 °C |
2.67 cc-mil/100 in²-24hr-atm @Temperature 73.4 °F |
at 0% r.h., Film; DIS 15105-1/-2 |
| 1.60 cc-mm/m²-24hr-atm @Temperature 23.0 °C |
4.06 cc-mil/100 in²-24hr-atm @Temperature 73.4 °F |
at 85% r.h., Film; DIS 15105-1/-2 | |
| Viscosity | 2.74e+6 cP @Temperature 260 °C |
2.74e+6 cP @Temperature 500 °F |
Melt Viscosity; DSM Method |
| 200000 cP @Shear Rate 1000 1/s, Temperature 280 °C |
200000 cP @Shear Rate 1000 1/s, Temperature 536 °F |
||
| 250000 cP @Shear Rate 1000 1/s, Temperature 260 °C |
250000 cP @Shear Rate 1000 1/s, Temperature 500 °F |
||
| 300000 cP @Shear Rate 1000 1/s, Temperature 240 °C |
300000 cP @Shear Rate 1000 1/s, Temperature 464 °F |
||
| 2.00e+6 cP @Shear Rate 0.100 1/s, Temperature 280 °C |
2.00e+6 cP @Shear Rate 0.100 1/s, Temperature 536 °F |
||
| 3.00e+6 cP @Shear Rate 0.100 1/s, Temperature 260 °C |
3.00e+6 cP @Shear Rate 0.100 1/s, Temperature 500 °F |
||
| 5.00e+6 cP @Shear Rate 0.100 1/s, Temperature 240 °C |
5.00e+6 cP @Shear Rate 0.100 1/s, Temperature 464 °F |
||
| Viscosity Measurement | 3.0 | 3.0 | RSV formic acid, 1g/100ml; DSM Method |
| Viscosity Test | 194 cm³/g | 194 cm³/g | Viscosity Number; ISO 307, 1157, 1628 |
| Thickness | 50.0 microns | 1.97 mil | Film |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 36.0 MPa | 5220 psi | parallel; ISO 527-3 |
| Film Elongation at Break, MD | 340 % | 340 % | parallel; ISO 527-3 |
| Modulus of Elasticity | 0.490 GPa | 71.1 ksi | Film; DSM-Method, 50 mm/min |
| Coefficient of Friction, Dynamic | 0.80 | 0.80 | Film; ISO 8295 |
| Coefficient of Friction, Static | 1.4 | 1.4 | Film; ISO 8295 |
| Tear Strength Test | 23 | 23 | Trouser Tear Resistance, parallel, Film; ISO 6383-1 |
| Film Tensile Strength at Break, MD | 96.0 MPa | 13900 psi | parallel; ISO 527-3 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 90.0 µm/m-°C | 50.0 µin/in-°F | ISO 11359-1/-2 |
| Specific Heat Capacity | 1.55 J/g-°C @Temperature 23.0 °C |
0.370 BTU/lb-°F @Temperature 73.4 °F |
|
| 2.25 J/g-°C @Temperature 20.0 - 150 °C |
0.538 BTU/lb-°F @Temperature 68.0 - 302 °F |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 85 % | 85 % | Film; DSM Method |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 270 °C | 518 °F | Extruder Temperature, Film |
| Die Temperature | 270 °C | 518 °F | |
| Roll Temperature | 110 °C | 230 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Extrusion Type | Cast Film | |
| Puncture Resistance | 1200 J/m | Film (DSM Method) |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics LNP LUBRICOMP DFL22 PC
- REXtac Rextac® RT 1215 Amorphous Polyalphaolefin (APAO)
- Inno-Comp INNOBATCH® PPH 6160 60% Talc Filled Polypropylene Homopolymer
- KYDEX® 5555 Low Heat Release Aviation Thermoforming Sheet
- Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed 1950°F (1070°C) + Aged 1400°F (760°C)
- Tisan TISAPET® 30% Glass Reinforced Polyethylene Terephthalate
- Loctite® 496 General Purpose Methyl Cyanoacrylate Bonding Adhesive
- ExxonMobil LL 8555.67 Rotational Molding Resin (discontinued **)
- Loctite® Durabond® M-21HP Epoxy Adhesive
Copyright © lookpolymers.com All Rights Reserved