- Crucible Steel CSM® S60V (440V) Tool Steel, AISI 440C Modified
Crucible Steel CSM® S60V (440V) Tool Steel, AISI 440C Modified
| Category | Metal , Ferrous Metal , Tool Steel |
| Manufacturer | Crucible Steel |
| Trade Name | CSM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Crucible Steel CSM® S60V (440V) Tool Steel, AISI 440C Modified.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
CPM S60V is a unique tool steel made by the Crucible Particle Metallurgy process. It is designed from a 440C stainless base analysis with added high carbon and vanadium for exceptionally good wear resistance.The exceptional wear resistance and good corrosion resistance of CPM S60V make it an excellent candidate to replace 440C and other corrosion and wear resistant materials, particularly where increased wear resistance is a primary concern.Information provided by Crucible Industries
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 7.47 g/cc | 0.270 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell C | 58 | 58 | Heat Treated at 1950°F then air cooled |
| 60 | 60 | Heat Treated at 1950°F then quenched | |
| 54 @Tempering Temp. 260 - 371 °C |
54 @Tempering Temp. 500 - 700 °F |
Heat Treated at 1950°F then air cooled and tempered | |
| 55 @Tempering Temp. 260 - 371 °C |
55 @Tempering Temp. 500 - 700 °F |
Heat Treated at 1950°F then quenched and tempered | |
| 56 @Tempering Temp. 204 °C |
56 @Tempering Temp. 400 °F |
Heat Treated at 1950°F then air cooled and tempered | |
| 56 @Tempering Temp. 316 - 371 °C |
56 @Tempering Temp. 600 - 700 °F |
Heat Treated at 2050°F then air cooled and tempered | |
| 58 @Tempering Temp. 204 °C |
58 @Tempering Temp. 400 °F |
Heat Treated at 2050°F then air cooled and tempered | |
| 58 @Tempering Temp. 204 °C |
58 @Tempering Temp. 400 °F |
Heat Treated at 1950°F then quenched and tempered | |
| 58 @Tempering Temp. 316 - 371 °C |
58 @Tempering Temp. 600 - 700 °F |
Heat Treated at 2050°F then quenched and tempered | |
| 60 @Tempering Temp. 204 °C |
60 @Tempering Temp. 400 °F |
Heat Treated at 2050°F then quenched and tempered | |
| Modulus of Elasticity | 207 GPa | 30000 ksi | |
| Charpy Impact | 16.3 J @Treatment Temp. 1070 °C |
12.0 ft-lb @Treatment Temp. 1950 °F |
hardened; C-notch |
| 21.7 J @Treatment Temp. 1010 °C |
16.0 ft-lb @Treatment Temp. 1850 °F |
hardened; C-notch |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 11.1 µm/m-°C @Temperature 21.1 - 204 °C |
6.14 µin/in-°F @Temperature 70.0 - 400 °F |
|
| 11.5 µm/m-°C @Temperature 21.1 - 316 °C |
6.37 µin/in-°F @Temperature 70.0 - 600 °F |
||
| 12.2 µm/m-°C @Temperature 21.1 - 593 °C |
6.79 µin/in-°F @Temperature 70.0 - 1100 °F |
||
| Thermal Conductivity | 1.40 W/m-K | 9.70 BTU-in/hr-ft²-°F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Carbon, C | 2.15 % | 2.15 % | |
| Chromium, Cr | 17 % | 17 % | |
| Iron, Fe | 73.5 % | 73.5 % | as balance |
| Manganese, Mn | 0.40 % | 0.40 % | |
| Molybdenum, Mo | 1.0 % | 1.0 % | |
| Silicon, Si | 0.40 % | 0.40 % | |
| Vanadium, V | 5.5 % | 5.5 % |
| Chemical Properties | Metric | English | Comments |
|---|---|---|---|
| Critical Temperature | 860 °C | 1580 °F |
Users viewing this material also viewed the following:
- MV Labs NA870 Na2CO4 Sodium oxalate
- Fibre Glast 1101 High-Strength General Purpose Epoxy Adhesive
- Borealis Bormed™ TD109CF Polypropylene Copolymer
- A. Schulman POLYBATCH™ XAMF-500-T Process Aid Concentrate, Concentrate Based In LLDPE
- 3M 1126 EMI Shielding Tape
- Arkema Group Orgalloy® LE 60XV Flexible Nylon Alloy (Conditioned)
- Azdel Plus R300-B01 30% Continuous Random Fiber Mat / PP Resin Matrix
- Axiall 2502 Rigid PVC, Extrusion
- Azoty Tarnow™ TARNOFORM 200 HI4 POM
Copyright © lookpolymers.com All Rights Reserved