Covestro Bayblend® R-FR 610 Polycarbonate/ABS Blend  (discontinued **)

Category	Polymer , Renewable/Recycled Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	EXW, FOB, CFR, CIF
Payment Terms	L/C, T/T, PayPal
Download PDF	Covestro Bayblend® R-FR 610 Polycarbonate/ABS Blend  (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

FR-recycled grades with 25% recycled content.Applications: Housings for office equipment, electrical engineering, computer sectors.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and has officially adopted its new name – Covestro. This product was discontinued prior to the separation.

Physical Properties	Metric	English	Comments
Density	1.18 g/cc	0.0426 lb/in³
Water Absorption	0.70 %	0.70 %	Saturation in water
Moisture Absorption at Equilibrium	0.20 %	0.20 %	Equilibrium at 50% RH
Water Absorption at Saturation	0.70 %	0.70 %
Melt Flow	20 g/10 min <br>@Load 5.00 kg,<br> Temperature 240 °C	20 g/10 min <br>@Load 11.0 lb,<br> Temperature 464 °F

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	55.0 MPa	7980 psi
Elongation at Break	40 %	40 %	Nominal
Elongation at Yield	4.0 %	4.0 %
Tensile Modulus	2.40 GPa	348 ksi

Thermal Properties	Metric	English
CTE, linear, Parallel to Flow	76.0 µm/m-°C <br>@Temperature 20.0 °C	42.2 µin/in-°F <br>@Temperature 68.0 °F
CTE, linear, Transverse to Flow	80.0 µm/m-°C <br>@Temperature 20.0 °C	44.4 µin/in-°F <br>@Temperature 68.0 °F
Deflection Temperature at 0.46 MPa (66 psi)	95.0 °C	203 °F
Deflection Temperature at 1.8 MPa (264 psi)	85.0 °C	185 °F
Vicat Softening Point	98.0 °C	208 °F
Flammability, UL94	V-0 <br>@Thickness 1.60 mm	V-0 <br>@Thickness 0.0630 in
Oxygen Index	33 %	33 %

Electrical Properties	Metric	English
Electrical Resistivity	1.00e+15 ohm-cm	1.00e+15 ohm-cm
Surface Resistance	>= 1.00e+15 ohm	>= 1.00e+15 ohm
Dielectric Constant	2.9 <br>@Frequency 1e+6 Hz	2.9 <br>@Frequency 1e+6 Hz
	3.0 <br>@Frequency 100 Hz	3.0 <br>@Frequency 100 Hz
Dielectric Strength	30.0 kV/mm	762 kV/in
Dissipation Factor	0.0030 <br>@Frequency 100 Hz	0.0030 <br>@Frequency 100 Hz
	0.0080 <br>@Frequency 1e+6 Hz	0.0080 <br>@Frequency 1e+6 Hz
Comparative Tracking Index	300 V	300 V