Cossa Polimeri ESTASTIR HI 0408 V0 Flame Retardant Polystyrene
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Flame Retardant |
| Manufacturer | Cossa Polimeri S.r.L. |
| Trade Name | ESTASTIR |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Cossa Polimeri ESTASTIR HI 0408 V0 Flame Retardant Polystyrene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Flame retardant class V0, PBDE free, good impact resistance, good thermal resistance, high light resistance, good processabilityInformation provided by Cossa Polimeri S.r.l.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.17 g/cc | 0.0423 lb/in³ | ASTM D 792 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ASTM D 955 |
| Melt Flow | 4.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
4.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 22.0 MPa | 3190 psi | ASTM D 638 |
| Tensile Strength, Yield | 28.0 MPa | 4060 psi | ASTM D 638 |
| Elongation at Break | 40 % | 40 % | ASTM D 638 |
| Flexural Modulus | 2.20 GPa | 319 ksi | ASTM D 790 |
| Izod Impact, Notched | 0.600 J/cm @Temperature 0.000 °C |
1.12 ft-lb/in @Temperature 32.0 °F |
ASTM D 638 |
| 0.800 J/cm @Temperature 23.0 °C |
1.50 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 91.0 °C @Load 5.00 kg |
196 °F @Load 11.0 lb |
50°C/hr; ASTM D 1525 |
| 99.0 °C @Load 0.999 kg |
210 °F @Load 2.20 lb |
50°C/hr; ASTM D 1525 | |
| Flammability, UL94 | V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
|
| V-0 @Thickness 3.20 mm |
V-0 @Thickness 0.126 in |
||
| Glow Wire Test | 960 °C | 1760 °F | I.E.C. 695-2-1 |
Users viewing this material also viewed the following:
- Multibase SILASTIC® Q7-4850 Dow-Corning Biomedical Grade Liquid Silicone Rubber
- Garlock GYLON® 3522 PTFE Diaphragm
- Techmer ES HiFill® PA6 GF55 HS L 55% Glass Filled
- Techmer ES HiFill® HIPS TM40 WT 40% Talc Filled
- Eurotec® Tecomid® NB50 NL IT PA6, impact modified, super tough, natural, extrusion grade
- Asahi Kasei Thermylene® P6-10FG-Y950 10% Glass Fiber Reinforced, Lubricated
- Beijing Ranger Chem PBT-201-G30 202 Environmental Protection Flame Retarding FR PBT
- Aaron Industries AAROPRENE® GFPP 2020 Glass Filled Polypropylene
- BLUESTAR 403HF-G30 PBT, 30% Glass Filled
Copyright © lookpolymers.com All Rights Reserved