- Cossa Polimeri ESTAPROP HK 1280 T8 Polypropylene, 40% Mineral Filled
Cossa Polimeri ESTAPROP HK 1280 T8 Polypropylene, 40% Mineral Filled
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Mineral Reinforced |
| Manufacturer | Cossa Polimeri S.r.L. |
| Trade Name | ESTAPROP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Cossa Polimeri ESTAPROP HK 1280 T8 Polypropylene, 40% Mineral Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PP homopolymer 40% mineral fillerExcellent physical and mechanical characteristics, good surface appearanceInformation provided by Cossa Polimeri S.r.l.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.25 g/cc | 0.0452 lb/in³ | ASTM D 792 |
| Linear Mold Shrinkage | 0.010 - 0.012 cm/cm | 0.010 - 0.012 in/in | ASTM D 955 |
| Melt Flow | 12 g/10 min @Load 2.16 kg, Temperature 230 °C |
12 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 21.0 MPa | 3050 psi | ASTM D 638 |
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | ASTM D 638 |
| Elongation at Break | 20 % | 20 % | ASTM D 638 |
| Tensile Modulus | 4.10 GPa | 595 ksi | ASTM D 638 |
| Flexural Modulus | 3.80 GPa | 551 ksi | ASTM D 790 |
| Izod Impact, Notched | 0.150 J/cm @Temperature -20.0 °C |
0.281 ft-lb/in @Temperature -4.00 °F |
ASTM D 638 |
| 0.200 J/cm @Temperature 0.000 °C |
0.375 ft-lb/in @Temperature 32.0 °F |
ASTM D 638 | |
| 0.300 J/cm @Temperature 23.0 °C |
0.562 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 72.0 °C | 162 °F | 120°C/hr; ASTM D 648 |
| Vicat Softening Point | 97.0 °C @Load 5.00 kg |
207 °F @Load 11.0 lb |
50°C/hr; ASTM D 1525 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
Users viewing this material also viewed the following:
- Nye Lubricants 740S (RL) Synthetic Oil
- Overview of materials for Nylon 66, 40% Glass Fiber Filled
- Lehmann & Voss LUVOCOM® 1105/GR/15/TF/15-2 PEEK, with PTFE, lubricant modified
- Indium Corp. Indalloy 26 Bismuth Solder Alloy
- Haynes 556® alloy, 10% cold reduction, 1065°C anneal for 5 minutes
- A. Schulman POLYFORT™ FPP 2122UV-M-31 Black, Talc Filled Copolymer Polypropylene
- Zeon Chemicals Zeonor® 1060R Cyclo Olefin Polymer
- ConocoPhillips Hydroclear Diamond Class® 32 AW Turbine Oil
- 3M 8992L Polyester Tape
Copyright © lookpolymers.com All Rights Reserved