Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Unreinforced, Flame Retardant |
Manufacturer | Cossa Polimeri S.r.L. |
Trade Name | ESTACARB |
Port | Shanghai port,China |
Trade Terms | FOB, CFR, CIF |
Payment Terms | L/C, T/T, Western Union |
Download PDF | Cossa Polimeri ESTACARB 1060 V0 HF Flame Retardant Polycarbonate.pdf ![]() |
Price | EMAIL US sales@lookpolymers.com |
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 1.20 g/cc | 0.0434 lb/in³ | ASTM D 792 |
Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D 955 |
Melt Flow | 10 g/10 min @Load 1.20 kg, Temperature 300 °C |
10 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D 1238 |
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 60.0 MPa | 8700 psi | ASTM D 638 |
Tensile Strength, Yield | 65.0 MPa | 9430 psi | ASTM D 638 |
Elongation at Break | >= 50 % | >= 50 % | ASTM D 638 |
Flexural Modulus | 2.50 GPa | 363 ksi | ASTM D 790 |
Izod Impact, Notched | 5.50 J/cm @Temperature 0.000 °C |
10.3 ft-lb/in @Temperature 32.0 °F |
ASTM D 638 |
6.00 J/cm @Temperature 23.0 °C |
11.2 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
Thermal Properties | Metric | English | Comments |
---|---|---|---|
Hot Ball Pressure Test | 135 °C | 275 °F | I.E.C. 335-1 |
Vicat Softening Point | 145 °C @Load 5.00 kg |
293 °F @Load 11.0 lb |
50°C/hr; ASTM D 1525 |
148 °C @Load 0.999 kg |
298 °F @Load 2.20 lb |
50°C/hr; ASTM D 1525 | |
Flammability, UL94 | V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
|
V-0 @Thickness 3.20 mm |
V-0 @Thickness 0.126 in |
||
Glow Wire Test | 960 °C | 1760 °F | I.E.C. 695-2-1 |