Cosmic Plastics K66 Long Glass Fiber Filled Iso Diallyl Phthalate Molding Compound
| Category | Polymer , Thermoset , Diallyl Phthalate (DAP) , Diallyl Phthalate (DAP) Molding Compound, Long Glass Fiber Filled , Filled/Reinforced Thermoset |
| Manufacturer | Cosmic Plastics |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Cosmic Plastics K66 Long Glass Fiber Filled Iso Diallyl Phthalate Molding Compound.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by the manufacturer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.82 g/cc | 0.0658 lb/in³ | |
| Apparent Bulk Density | 0.300 g/cc | 0.0108 lb/in³ | |
| Water Absorption | 0.25 % | 0.25 % | 48 hrs, 50°C |
| Linear Mold Shrinkage | 0.0010 - 0.0040 cm/cm | 0.0010 - 0.0040 in/in | typical. |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 41.0 - 69.0 MPa | 5950 - 10000 psi | |
| Flexural Strength | 103 MPa | 14900 psi | |
| Compressive Strength | 186 MPa | 27000 psi | |
| Izod Impact, Notched | 2.40 J/cm | 4.50 ft-lb/in |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 24.0 µm/m-°C @Temperature 20.0 °C |
13.3 µin/in-°F @Temperature 68.0 °F |
|
| Deflection Temperature at 1.8 MPa (264 psi) | 260 °C | 500 °F | Heat Distortion temperature |
| Flammability, UL94 | V-0 @Thickness 3.20 mm |
V-0 @Thickness 0.126 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | >= 1.00e+17 ohm-cm | >= 1.00e+17 ohm-cm | |
| Surface Resistance | >= 1.00e+17 ohm | >= 1.00e+17 ohm | |
| Dielectric Constant | 3.9 @Frequency 1e+6 Hz |
3.9 @Frequency 1e+6 Hz |
Wet |
| 4.1 @Frequency 1000 Hz |
4.1 @Frequency 1000 Hz |
Wet | |
| Dielectric Strength | 16.0 kV/mm | 406 kV/in | Wet, Step by Step |
| Dissipation Factor | 0.0090 @Frequency 1000 Hz |
0.0090 @Frequency 1000 Hz |
Wet |
| 0.013 @Frequency 1e+6 Hz |
0.013 @Frequency 1e+6 Hz |
Wet | |
| Arc Resistance | 180 sec | 180 sec |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 135 - 165 °C | 275 - 329 °F | Molding temperature |
Users viewing this material also viewed the following:
- Polykemi AB POLYlux 3809SLB PC/PBT-Blend, Paintable
- LG Chemical LUCEL EC-605B Electrically Conductive POM, 5% Carbon Black Filled
- SABIC Innovative Plastics LNP LUBRICOMP EFL24P PEI
- Techmer ES Electrafil® NY-7/EC NAT PA6
- Teknor Apex APEX® 84217 Polyvinyl Chloride, Flexible
- Wellman Wellamid® FR22F-N Flame Retardant Nylon 66, Lubricated
- A. Schulman INVISION™ VX-5060UI INVISIONTMSoft Touch Polyolefin Thermoplastic
- Eliokem Sunigum® P7395 Acrylate Terpolymer
- Borealis Borstar® HE6063 Natural Bimodal HD Polyethylene Compound for Jacketing of Communication and Power Cables
Copyright © lookpolymers.com All Rights Reserved