Cosmic Plastics 6120 Short Glass Fiber Filled Ortho Diallyl Phthalate Molding Compound
| Category | Polymer , Thermoset , Diallyl Phthalate (DAP) , Diallyl Phthalate (DAP) Molding Compound, Short Glass Fiber Filled , Filled/Reinforced Thermoset |
| Manufacturer | Cosmic Plastics |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Cosmic Plastics 6120 Short Glass Fiber Filled Ortho Diallyl Phthalate Molding Compound.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by the manufacturer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.81 g/cc | 0.0654 lb/in³ | |
| Apparent Bulk Density | 0.720 g/cc | 0.0260 lb/in³ | |
| Water Absorption | 0.25 % | 0.25 % | 48 hrs, 50°C |
| Linear Mold Shrinkage | 0.0010 - 0.0040 cm/cm | 0.0010 - 0.0040 in/in | typical. |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 41.0 - 69.0 MPa | 5950 - 10000 psi | |
| Flexural Strength | 97.0 MPa | 14100 psi | |
| Compressive Strength | 172 MPa | 24900 psi | |
| Izod Impact, Notched | 0.450 J/cm | 0.843 ft-lb/in |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 25.0 µm/m-°C @Temperature 20.0 °C |
13.9 µin/in-°F @Temperature 68.0 °F |
|
| Deflection Temperature at 1.8 MPa (264 psi) | 260 °C | 500 °F | Heat Distortion temperature |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | >= 1.00e+17 ohm-cm | >= 1.00e+17 ohm-cm | |
| Surface Resistance | >= 1.00e+17 ohm | >= 1.00e+17 ohm | |
| Dielectric Constant | 4.4 @Frequency 1000 Hz |
4.4 @Frequency 1000 Hz |
Wet |
| 4.4 @Frequency 1e+6 Hz |
4.4 @Frequency 1e+6 Hz |
Wet | |
| Dielectric Strength | 13.0 kV/mm | 330 kV/in | Wet, Step by Step |
| Dissipation Factor | 0.012 @Frequency 1000 Hz |
0.012 @Frequency 1000 Hz |
Wet |
| 0.015 @Frequency 1e+6 Hz |
0.015 @Frequency 1e+6 Hz |
Wet | |
| Arc Resistance | 135 sec | 135 sec |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 135 - 165 °C | 275 - 329 °F | Molding temperature |
Users viewing this material also viewed the following:
- MV Labs RH700 Rh(NO3)3 Rhodium nitrate
- Intercontinental Polymers 1128 Bicomponent PBT/PET Fiber Type - 1.8 Denier X 3 Inches
- Misumi ANP79 Aluminum Alloy
- Möller Medical PolySkin 98 S NanoCoating
- Karina 752-12/6-Y-BZ Ruby Red PVC Compound
- Techmer ES Plastiblend® PA6 L N BK MB Nylon 6
- Chevron Phillips MarFlex® D139DK Metallocene Linear Low Density Polyethylene, Blown Film
- ExxonMobil Isopar™ K (EU) Isoparaffin Fluid
- ArcelorMittal FB 540 Hot rolled ferrite-bainite steel
- SABIC Innovative Plastics LNP THERMOCOMP 2X04505 ETFE
Copyright © lookpolymers.com All Rights Reserved