Styrolution Polystyrol 145 D PS
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Molded, Unreinforced |
| Manufacturer | Styrolution |
| Trade Name | Polystyrol |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styrolution Polystyrol 145 D PS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Polystyrol 145 D is a medium strength, easy flowing general purpose grade, suitable for blending with impact modified Polystyrol.Applications: In blends with high impact polystyrene especially suitable for FFS-sheets.Information provided by STYROLUTION, which is a joint venture between BASF and INEOS
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.046 g/cc | 0.03779 lb/in³ | ISO 1183 |
| Water Absorption | <= 0.10 % | <= 0.10 % | ISO 62 |
| Moisture Absorption at Equilibrium | <= 0.10 % | <= 0.10 % | 23°C/50% RH; ISO 62 |
| Melt Flow | 15.69 g/10 min @Load 5.00 kg, Temperature 200 °C |
15.69 g/10 min @Load 11.0 lb, Temperature 392 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 150 MPa | 21800 psi | ISO 2039-1 |
| Tensile Strength at Break | 44.0 MPa | 6380 psi | ISO 527-1/-2 |
| Elongation at Break | 2.0 % | 2.0 % | ISO 527-1/-2 |
| Tensile Modulus | 3.30 GPa | 479 ksi | ISO 527-1/-2 |
| Flexural Strength | 70.0 MPa | 10200 psi | ISO 178 |
| Poissons Ratio | 0.22 | 0.22 | Calculated |
| Shear Modulus | 1.35 GPa | 196 ksi | ISO 6721-2 |
| Charpy Impact Unnotched | <= 2.50 J/cm² | <= 11.9 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 0.300 J/cm² | 1.43 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 °C | 190 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | ISO 75-1/-2 |
| Vicat Softening Point | 88.0 °C | 190 °F | VST/B/50; ISO 306 |
| 96.0 °C | 205 °F | VST/A/120; ISO 306 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+16 ohm-cm | >= 1.00e+16 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+14 ohm | >= 1.00e+14 ohm | IEC 60093 |
| Dielectric Constant | 2.5 @Frequency 1.00e+6 Hz |
2.5 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 2.5 @Frequency 100 Hz |
2.5 @Frequency 100 Hz |
IEC 60250 | |
| Dielectric Strength | 135 kV/mm | 3430 kV/in | K20/P50; IEC 60243-1 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 210 - 240 °C | 410 - 464 °F | Flat film |
| 180 - 280 °C | 356 - 536 °F | Injection Molding | |
| Mold Temperature | 10.0 - 60.0 °C | 50.0 - 140 °F | Injection Molding |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Crystal Clear 00013 | |
| Commercial Status | Europe | |
| Primary Processing Technique | Injection Molding and Extrusion |
Users viewing this material also viewed the following:
- MetalTek MTEK 76-6-18 HI LEAD Cast UNS C94100 Bearing Bronze
- Garlock 9200 Nitrile Rubber Gasketing, Nylon Insert
- SK Chemicals SKYPEL G130D General Grade
- Teknor Apex Uniprene® UN-7100-87 Thermoplastic Vulcanizate
- Esstech V-117-1112 Barium Borosilicate Glass
- Fainplast Compounds GK 83 Flexible PVC, Flame Retardant Sheathing Lead Free
- DuPont Performance Polymers Zytel® FR50 NC010A Nylon 66 (Unverified Data**)
- LG Chemical MA201 ABS, Low Gloss
- Eastman Tenite Butyrate 581A3720016 Clear, Trsp Cellulose Acetate Butyrate (discontinued **)
Copyright © lookpolymers.com All Rights Reserved