- Polyphthalamide (PPA), 50% Glass Fiber Reinforced
- Clariant Renol PPA1100G50 Polyphthalamide, 50% Glass Fiber
Clariant Renol PPA1100G50 Polyphthalamide, 50% Glass Fiber
| Category | Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 50% Glass Fiber Reinforced |
| Manufacturer | Clariant |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Clariant Renol PPA1100G50 Polyphthalamide, 50% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Clariant Masterbatches
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.64 g/cc | 1.64 g/cc | ASTM D792 |
| Filler Content | 50 % | 50 % | ASTM D2584 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 24.8 MPa | 3600 psi | ASTM D638 |
| Elongation at Break | 2.0 - 3.0 % | 2.0 - 3.0 % | ASTM D638 |
| Flexural Yield Strength | 365 MPa | 53000 psi | ASTM D790 |
| Flexural Modulus | 17.2 GPa | 2500 ksi | ASTM D790 |
| Izod Impact, Notched | 1.17 J/cm @Temperature 22.8 °C |
2.20 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 282 °C | 540 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 302 - 329 °C | 575 - 625 °F | |
| Mold Temperature | 135 - 163 °C | 275 - 325 °F | |
| Dry Time | 6 hour @Temperature 79.4 °C |
6 hour @Temperature 175 °F |
to ensure moisture level is less than 0.5% |
| Injection Pressure | 41.4 - 74.5 MPa | 6000 - 10800 psi | Secondary |
| 68.9 - 124 MPa | 10000 - 18000 psi | Initial | |
| Back Pressure | 0.345 - 1.72 MPa | 50.0 - 250 psi | |
| Shot Size | 30 - 80 % | 30 - 80 % | |
| Screw Speed | 20 - 100 rpm | 20 - 100 rpm |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Wire & Cable W2301 Polyvinyl Chloride, Flexible (PVC, Flexible)
- Nilit FRIANYL A63 H-SG50 Nylon 6.6 for injection molding, 50% mineral filled
- Lehmann & Voss LUVOCOM® 50-7289/V2 Polycarbonate, with carbon fiber and PTFE
- Flint Hills P4C5T-013 Homopolymer Polypropylene
- Materion Beryllium Copper Alloy 25 Tube; HT (TH04) Temper; over 9.5 to 25.4 mm o.d. (UNS C17200)
- Solvay Specialty Polymers Amodel® AS-1133 HS Polyphthalamide (PPA), 33% Glass Fiber (Conditioned)
- Shandong Rike Chemical HELIâ„¢ K-120N PVC Processing Aid Series (PA)
- Teknor Apex Monprene® MP-2730B Thermoplastic Elastomer
- Spartech APET SP4110 Copolyester Sheet
Copyright © lookpolymers.com All Rights Reserved