Chosun Refractories HSC-18 Dense and High-Strength Castable, Credens
| Category | Ceramic , Oxide , Aluminum Oxide |
| Manufacturer | Chosun Refractories |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chosun Refractories HSC-18 Dense and High-Strength Castable, Credens.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Chosun Refractories via Korea Institute of Ceramic Engineering and Technology (KICET).
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Rupture | 0.01962 GPa @Temperature 110 °C, Time 86400 sec |
2.846 ksi @Temperature 230 °F, Time 24.0 hour |
|
| 0.023544 GPa @Temperature 1000 °C, Time 10800 sec |
3.4148 ksi @Temperature 1830 °F, Time 3.00 hour |
||
| 0.034335 GPa @Temperature 1500 °C, Time 10800 sec |
4.9799 ksi @Temperature 2730 °F, Time 3.00 hour |
||
| Compressive Strength | 78.5 MPa @Temperature 110 °C, Time 86400 sec |
11400 psi @Temperature 230 °F, Time 24.0 hour |
Cold Crushing Strength |
| 88.3 MPa @Temperature 1000 °C, Time 10800 sec |
12800 psi @Temperature 1830 °F, Time 3.00 hour |
Cold Crushing Strength | |
| 118 MPa @Temperature 1500 °C, Time 10800 sec |
17100 psi @Temperature 2730 °F, Time 3.00 hour |
Cold Crushing Strength |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 1800 °C | 3270 °F | limited |
| Shrinkage | -0.300 % @Temperature 1500 °C, Time 10800 sec |
-0.300 % @Temperature 2730 °F, Time 3.00 hour |
|
| -0.0600 % @Temperature 110 °C, Time 86400 sec |
-0.0600 % @Temperature 230 °F, Time 24.0 hour |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Al2O3 | 90 % | 90 % | |
| CaO | 2.0 % | 2.0 % |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 120 - 600 min | 2.00 - 10.0 hour | Setting Time |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Installation Method | Vibrating, Casting | |
| Material Required for Estimating(kg/?) | 3,200 | |
| Water Required for Casting(%) | 4.5 |
Users viewing this material also viewed the following:
- Polykemi AB POLYshine PBT D221 QF30 PBT, Glass and Mineral Reinforced
- PolyOne Geon™ Vinyl Flexible 90212 Polyvinyl Chloride, Flexible (PVC, Flexible)
- Johnson Matthey HPP Platinum Jewelry Alloy
- Shakespeare WonderThread® SN-40 ultra soft TEX# 8 Nylon Industrial Sewing Thread
- A. Schulman POLYFORT™ FPP 892E Extrusion and Blow Molding Grade Homopolymer Polypropylene
- DSM Stanyl® TC155 PA46 FR(17)
- E-Polymers TEKAMID® H14ST Super Toughness PA/ABS Alloy
- Pyrotek AFB-2300 HT Structural Board
- ExxonMobil LL 8460 Rotational Molding Resin (discontinued **)
Copyright © lookpolymers.com All Rights Reserved