| Category | Ceramic |
| Manufacturer | Chosun Refractories |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chosun Refractories CT-140S Fireclay Castables.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Chosun Refractories via Korea Institute of Ceramic Engineering and Technology (KICET).
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Rupture | 0.002943 - 0.006867 GPa @Temperature 1000 °C, Time 10800 sec |
0.4269 - 0.9960 ksi @Temperature 1830 °F, Time 3.00 hour |
|
| 0.002943 - 0.007848 GPa @Temperature 1350 °C, Time 10800 sec |
0.4269 - 1.138 ksi @Temperature 2460 °F, Time 3.00 hour |
||
| 0.003924 - 0.008829 GPa @Temperature 110 °C, Time 86400 sec |
0.5691 - 1.281 ksi @Temperature 230 °F, Time 24.0 hour |
||
| Compressive Strength | 19.6 - 29.4 MPa @Temperature 1000 °C, Time 10800 sec |
2840 - 4270 psi @Temperature 1830 °F, Time 3.00 hour |
Cold Crushing Strength |
| 24.5 - 34.3 MPa @Temperature 1350 °C, Time 10800 sec |
3560 - 4980 psi @Temperature 2460 °F, Time 3.00 hour |
Cold Crushing Strength | |
| 29.4 - 39.2 MPa @Temperature 110 °C, Time 86400 sec |
4270 - 5690 psi @Temperature 230 °F, Time 24.0 hour |
Cold Crushing Strength |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 0.5234 W/m-K @Temperature 260 °C |
3.627 BTU-in/hr-ft²-°F @Temperature 500 °F |
|
| 0.65137 W/m-K @Temperature 540 °C |
4.5132 BTU-in/hr-ft²-°F @Temperature 1000 °F |
||
| 0.77931 W/m-K @Temperature 800 °C |
5.3997 BTU-in/hr-ft²-°F @Temperature 1470 °F |
||
| Maximum Service Temperature, Air | 1400 °C | 2550 °F | limited |
| Shrinkage | -1.20 % @Temperature 1350 °C, Time 10800 sec |
-1.20 % @Temperature 2460 °F, Time 3.00 hour |
|
| -0.0900 % @Temperature 110 °C, Time 86400 sec |
-0.0900 % @Temperature 230 °F, Time 24.0 hour |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Al2O3 | 43 % | 43 % | |
| SiO2 | 44 % | 44 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Installation Method | Casting, Troweling | |
| Material Required for Estimating(kg/?) | 2,000 | |
| Water Required for Casting(%) | 11.5 |
Users viewing this material also viewed the following:
- Dielectric Polymers NT-4511 High Temperature Tape (discontinued **)
- Gromax BTE45-DN00N1 Nylon 6 (Conditioned)
- Momentive Performance Materials Siloprenâ„¢ LSR 3286/70 Liquid Silicone Rubber - Self-Lubricating / Low Compression Set
- SABIC Innovative Plastics LNP LUBRICOMP RFN14 PA 66
- Solvay SIPOMER® PAM-200 Phosphate Esters of Ppg Monomethacrylate
- Borealis Bormed™ LE6603-PH LDPE for Healthcare Applications
- Dow LDPE 752A Low Density Polyethylene, Film Grade
- Clariant Renol PA111 Nylon 66, General Purpose
- DuPont Performance Polymers Zytel® 101F BKB009 Nylon 66 (Unverified Data**)
- Haynes 625 alloy, 50% cold reduction
Copyright © lookpolymers.com All Rights Reserved