Chosun Refractories CSN-309T Plate Brick
| Category | Ceramic , Oxide , Aluminum Oxide |
| Manufacturer | Chosun Refractories |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chosun Refractories CSN-309T Plate Brick.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Chosun Refractories via Korea Institute of Ceramic Engineering and Technology (KICET).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 3.05 - 3.15 g/cc | 0.110 - 0.114 lb/in³ | |
| Porosity | 2.0 - 5.0 % | 2.0 - 5.0 % |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Rupture | <= 0.00981 GPa @Temperature 1400 °C |
<= 1.42 ksi @Temperature 2550 °F |
|
| Compressive Strength | <= 127 MPa | <= 18500 psi | Cold Crushing Strength |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 8.00 - 10.0 µm/m-°C @Temperature 1000 °C |
4.44 - 5.56 µin/in-°F @Temperature 1830 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Al2O3 | 75 - 79 % | 75 - 79 % | |
| Carbon, C | 8.0 - 11 % | 8.0 - 11 % | |
| ZrO2 | 5.0 - 7.0 % | 5.0 - 7.0 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Remarks | Tar impregnated, Spalling resistance |
Users viewing this material also viewed the following:
- NOVA Chemicals Sclair® 17A Butene HDPE Film Resin
- Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 1.7 mm thick sheet
- Shandong Rike Chemical HELIâ„¢ HL-530 PVC Foaming Regulator
- SABIC Innovative Plastics LNP STAT-LOY 9X07438 ASA+PC
- Techmer ES Plastiblend® PA6 SF76 L
- Teknor Apex APEX® 130-P Polyvinyl Chloride, Flexible
- Master Bond EP39-2 Fast Curing Optically Clear Two Component Epoxy System
- Daikin DAI-EL G-781 Fluoroelastomer Copolymer, Bisphenol Curable Grade, 66% Fluorine Content
- 3M Scotch® 862 Reinforced Strapping Tape
Copyright © lookpolymers.com All Rights Reserved