- Chevron Phillips Marlex® HHM TR-166 Polyethylene, Film Grade; HDPE (discontinued **)
Chevron Phillips Marlex® HHM TR-166 Polyethylene, Film Grade; HDPE (discontinued **)
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Film Grade |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chevron Phillips Marlex® HHM TR-166 Polyethylene, Film Grade; HDPE
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
FDA approved.Data provided by the manufacturer
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.963 g/cc | 0.0348 lb/in³ | ASTM D1505 |
| Thickness | 25.4 microns | 1.00 mil | |
| Melt Flow | 6.0 g/10 min | 6.0 g/10 min | Condition 190/2.16; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 24.0 MPa | 3480 psi | Cast Film; ASTM D638 |
| Film Tensile Strength at Yield, TD | 25.0 MPa | 3630 psi | Cast Film; ASTM D638 |
| Film Elongation at Break, MD | 625 % | 625 % | Cast film; ASTM D638 |
| Film Elongation at Break, TD | 700 % | 700 % | Cast film; ASTM D638 |
| Elmendorf Tear Strength MD | 55 g | 55 g | Cast Film; ASTM D1922 |
| Elmendorf Tear Strength TD | 65 g | 65 g | Cast Film; ASTM D1922 |
| Elmendorf Tear Strength, MD | 2.17 g/micron | 55.0 g/mil | 1 mil; Cast Film; ASTM D1922 |
| Elmendorf Tear Strength, TD | 2.56 g/micron | 65.0 g/mil | 1 mil; Cast Film; ASTM D1922 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 2.33 @Frequency 100000 Hz |
2.33 @Frequency 100000 Hz |
ASTM D1531 |
| Dielectric Strength | 20.0 kV/mm @Thickness 3.17 mm |
508 kV/in @Thickness 0.125 in |
ASTM D149 |
| Dissipation Factor | >= 0.00010 @Frequency 100000 Hz |
>= 0.00010 @Frequency 100000 Hz |
ASTM D1531 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 193 - 232 °C | 379 - 450 °F | Stock Temperature |
Users viewing this material also viewed the following:
- Polymax® Maxelast® P3870H TPE, PP Overmold or Standalone use
- Network Polymers 351 Polystyrene
- Iran Petrochemical (PCC) MF3313 High Density Polyethylene
- A. Schulman SCHULAMID® 66 MV3H Unreinforced Nylon 6/6
- DuPont™ Nomex® 410 Paper, 2 mil Nominal Thickness
- Chosun Refractories SF31S Hard Fireclay brick
- Fainplast Compounds MPH 62 Medical Flexible PVC, Extrusion
- Arlon 0.008" (0.2032 mm) Thermabond®-45 Uncured Silicone (99720W008)
Copyright © lookpolymers.com All Rights Reserved