- High Density Polyethylene (HDPE), Film Grade
- Chevron Phillips Marlex® HHM TR-144 Polyethylene, Film Grade; HDPE (discontinued **)
Chevron Phillips Marlex® HHM TR-144 Polyethylene, Film Grade; HDPE (discontinued **)
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Film Grade |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chevron Phillips Marlex® HHM TR-144 Polyethylene, Film Grade; HDPE
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
FDA approved.Data provided by the manufacturer
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.947 g/cc | 0.0342 lb/in³ | ASTM D1505 |
| Moisture Vapor Transmission | 0.200 cc-mm/m²-24hr-atm | 0.508 cc-mil/100 in²-24hr-atm | ASTM E96 |
| Oxygen Transmission | 59.0 cc-mm/m²-24hr-atm | 150 cc-mil/100 in²-24hr-atm | ASTM D1434 |
| Thickness | 25.4 microns | 1.00 mil | |
| Melt Flow | 0.18 g/10 min | 0.18 g/10 min | Condition 190/2.16; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 24.0 MPa | 3480 psi | Blown film; ASTM D638 |
| Film Tensile Strength at Yield, TD | 26.0 MPa | 3770 psi | Blown film; ASTM D638 |
| Film Elongation at Break, MD | 480 % | 480 % | Blown film; ASTM D638 |
| Film Elongation at Break, TD | 640 % | 640 % | Blown film; ASTM D638 |
| Flexural Modulus | 1.103 GPa | 160.0 ksi | ASTM D790 |
| Elmendorf Tear Strength MD | 23 g | 23 g | Blown Film; ASTM D1922 |
| Elmendorf Tear Strength TD | 330 g | 330 g | Blown Film; ASTM D1922 |
| Elmendorf Tear Strength, MD | 0.906 g/micron | 23.0 g/mil | 1 mil; Blown Film; ASTM D1922 |
| Elmendorf Tear Strength, TD | 13.0 g/micron | 330 g/mil | 1 mil; Blown Film; ASTM D1922 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 2.33 @Frequency 100000 Hz |
2.33 @Frequency 100000 Hz |
ASTM D1531 |
| Dielectric Strength | 20.0 kV/mm @Thickness 3.17 mm |
508 kV/in @Thickness 0.125 in |
ASTM D149 |
| Dissipation Factor | >= 0.00010 @Frequency 100000 Hz |
>= 0.00010 @Frequency 100000 Hz |
ASTM D1531 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 193 - 216 °C | 379 - 421 °F | Stock Temperature |
Users viewing this material also viewed the following:
- MV Labs FE870 (NH4)3Fe(C2O4)3·3H2O Ammonium iron(III) oxalate
- SABIC Innovative Plastics LNP LUBRICOMP CGI11 PS (Europe-Africa-Middle East)
- Gouda Vuurvast B Sp Dense Refractory Brick
- Lubrizol Estane® T465A Thermoplastic Polyurethane
- Tisan TISESTER® UNR Polybutylene Terephthalate
- Braskem F1000HC Homopolymer Polypropylene
- Adamas Adalon® 902 PTFE, 1% Conductive filler
- Addcomp ADD-VANCE® NU 795 Nucleation Masterbatch, PP based
- E-Polymers SEPAZ® C130HS 30% Glass Fiber Reinforced High Temperature Stabilized LCP Resin
- Azdel SuperLite® SL551400-100 PP Resin Matrix / 55% Glass Fiber (3 mm Molded Thickness)
Copyright © lookpolymers.com All Rights Reserved