Chevron Phillips Marlex® 1409 Injection Molding Resin (discontinued **)

Category	Polymer , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Molded
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Chevron Phillips Marlex® 1409 Injection Molding Resin (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Resin Type: Homopolymer; ASTM D 4976 Classification: PE 111, A 22200Characteristics: Good Flexibility, Excellent Flow, Excellent Warping Resistance, Excellent Mold Release, Moderate ESCRApplications:Lids and Overcaps for Dry or Oil-Free Products, Masterbatch Base ResinData provided by Chevron Chemical.

Physical Properties	Metric	English	Comments
Density	0.925 g/cc	0.0334 lb/in³	ASTM D1505
Melt Flow	50 g/10 min @Load 2.16 kg, Temperature 190 °C	50 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D 1238

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	54	54	ASTM D2240
Tensile Strength, Ultimate	11.0 MPa	1600 psi	ASTM D638
Tensile Strength, Yield	11.0 MPa	1600 psi	ASTM D638
Elongation at Break	>= 110 %	>= 110 %	ASTM D638
Flexural Modulus	0.193 GPa	28.0 ksi	3 pt. secant; ASTM D790
	0.269 GPa	39.0 ksi	3 pt. Tangent; ASTM D790

Thermal Properties	Metric	English	Comments
Vicat Softening Point	92.0 °C	198 °F	ASTM D1525
Brittleness Temperature	-14.0 °C	6.80 °F	ASTM D746