Chevron Phillips HiD® 9662 HDPE Blown Film Resin (discontinued **)

Category	Polymer , Film , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Film Grade
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Chevron Phillips HiD® 9662 HDPE Blown Film Resin (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Resin Type: Linear Polyethylene HomopolymerCharacteristics: Unique Molecular Architecture Gives Outstanding Moisture Barrier Properties, Excellent Film Strength and Toughness for a Homopolymer, Gives Paper-like Film Texture, Embosses Extremely Well, Draws to Very Thin Gauges, Excellent Heat Seal StrengthApplications: Food Packaging, Coextrusions, Tissue Paper Replacement, Deli Wrap, Moisture Barrier Films.Film properties below based on film thickness of 25.4 µm.Data provided by Chevron Chemical.

Physical Properties	Metric	English	Comments
Density	0.962 g/cc	0.0348 lb/in³	ASTM D1505
Moisture Vapor Transmission	0.100 cc-mm/m²-24hr-atm	0.254 cc-mil/100 in²-24hr-atm	ASTM F1249
Melt Flow	1.05 g/10 min	1.05 g/10 min	Condition E; ASTM D 1238

Mechanical Properties	Metric	English	Comments
Film Elongation at Break, MD	490 %	490 %	ASTM D882
Film Elongation at Break, TD	550 %	550 %	ASTM D882
Secant Modulus, MD	1.10 GPa	160 ksi	ASTM D882
Secant Modulus, TD	1.20 GPa	174 ksi	ASTM D882
Elmendorf Tear Strength, MD	0.748 g/micron	19.0 g/mil	Notched; ASTM D1922
Elmendorf Tear Strength, TD	8.27 g/micron	210 g/mil	ASTM D1922
Dart Drop	1.40 g/micron	35.6 g/mil	1.5 in. dart/26 in. drop height; ASTM D 1709
Film Tensile Strength at Break, MD	42.0 MPa	6090 psi	ASTM D882
Film Tensile Strength at Break, TD	26.0 MPa	3770 psi	ASTM D882

Processing Properties	Metric	English	Comments
Melt Temperature	210 °C	410 °F