Chevron Phillips 5658 LDPE Shrink and Bundling Film Resin (discontinued **)

Category	Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Chevron Phillips 5658 LDPE Shrink and Bundling Film Resin (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Resin Type: HomopolymerCharacteristics: Good Impact Strength, Good Abrasion and Tear Resistance, Good Sealing Properties, No Slip, Medium Antiblock, Easy OpenabilityApplications:Shrink Wrap, Bundling ApplicationsProcessing Conditions: Extruder 6.35 cm. Screw L/D Ratio 24:1. Die Opening 0.0762 cm. Blow-Up Ratio 2:1.Film properties below based on film thickness of 31.8 µm.Data provided by Chevron Chemical.

Physical Properties	Metric	English	Comments
Density	0.922 g/cc	0.0333 lb/in³	ASTM D1505
Melt Flow	0.80 g/10 min	0.80 g/10 min	Condition E; ASTM D 1238

Mechanical Properties	Metric	English	Comments
Secant Modulus, MD	0.170 GPa	24.7 ksi	ASTM D882
Secant Modulus, TD	0.180 GPa	26.1 ksi	ASTM D882
Coefficient of Friction	>= 1.0	>= 1.0	ASTM D1894
Dart Drop	6.30 g/micron	160 g/mil	F<sub>50</sub>; 1.5 in. dart/26 in. drop height; ASTM D 1709

Optical Properties	Metric	English	Comments
Haze	8.5 %	8.5 %	ASTM D2457
Gloss	50 %	50 %	at 45°. ASTM D 2457
	80 %	80 %	at 60°. ASTM D 2457

Processing Properties	Metric	English	Comments
Melt Temperature	210 °C	410 °F