Chesterton ARC NVE VC Vinyl Ester Sealer
| Category | Polymer , Thermoset , Vinyl Ester |
| Manufacturer | Chesterton |
| Trade Name | ARC NVE VC |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chesterton ARC NVE VC Vinyl Ester Sealer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: ARC NVE VC (Veil Coat) is a two-component, modified epoxy novolac vinyl ester sealer coat formulated for application by brush, roller or spray at 0.15-0.25 mm (0.07-0.010”) wet film thickness. It is used either to seal the NVE TC (Top Coat) or as a stand alone thin film chemical resistant barrier for concrete in chemical immersion applications. Benefits:User friendly consistency makes installation and finishing fast and easy.Seals surface for ease of cleaningInformation provided by Chesterton
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | Cured |
| Volatile Organic Compounds (VOC) Content | 70 g/l | 70 g/l | EPA 24 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Adhesive Bond Strength | >= 3.80 MPa | >= 551 psi | ASTM D4541 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 130 °C | 266 °F | Wet |
| 200 °C | 392 °F | Dry |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 60.0 min @Temperature 26.0 °C |
1.00 hour @Temperature 78.8 °F |
Foot Traffic |
| 60.0 min @Temperature 26.0 °C |
1.00 hour @Temperature 78.8 °F |
Light Load | |
| 60.0 min @Temperature 26.0 °C |
1.00 hour @Temperature 78.8 °F |
Full Load | |
| 90.0 min @Temperature 21.0 °C |
1.50 hour @Temperature 69.8 °F |
Foot Traffic | |
| 90.0 min @Temperature 21.0 °C |
1.50 hour @Temperature 69.8 °F |
Light Load | |
| 120 min @Temperature 21.0 °C |
2.00 hour @Temperature 69.8 °F |
Full Load | |
| 150 min @Temperature 16.0 °C |
2.50 hour @Temperature 60.8 °F |
Foot Traffic | |
| 180 min @Temperature 16.0 °C |
3.00 hour @Temperature 60.8 °F |
Light Load | |
| 240 min @Temperature 10.0 °C |
4.00 hour @Temperature 50.0 °F |
Foot Traffic | |
| 240 min @Temperature 16.0 °C |
4.00 hour @Temperature 60.8 °F |
Full Load | |
| 360 min @Temperature 10.0 °C |
6.00 hour @Temperature 50.0 °F |
Light Load | |
| 480 min @Temperature 10.0 °C |
8.00 hour @Temperature 50.0 °F |
Full Load | |
| 960 min @Temperature 26.0 °C |
16.0 hour @Temperature 78.8 °F |
Full Chemical | |
| 1440 min @Temperature 21.0 °C |
24.0 hour @Temperature 69.8 °F |
Full Chemical | |
| 1680 min @Temperature 16.0 °C |
28.0 hour @Temperature 60.8 °F |
Full Chemical | |
| 1920 min @Temperature 10.0 °C |
32.0 hour @Temperature 50.0 °F |
Full Chemical |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Gray | |
| Red |
Users viewing this material also viewed the following:
- PolyOne Maxxam™ PPR-20G Black Polypropylene Homopolymer (PP Homopolymer)
- Lotte Chemical Titan TITANZEX® HF7000 High density polyethylene
- Monmouth Rubber & Plastics Durafoamâ„¢ C41NBR Nitrile Rubber
- SABIC Innovative Plastics LNP THERMOCOMP OCF62 PPS - Branched
- Teknor Apex APEX® 4303 Polyvinyl Chloride Compound
- SABIC Innovative Plastics Noryl FXN2090H PPE+HIPS
- A. Schulman POLYFORT™ FPP 2496 Injection Molding Grade, Mineral Fortified Polypropylene
- Dow Corning SYL-OFF® SL 10 RELEASE MODIFIER
- Clariant Renol PPSP0006HW Polypropylene Homopolymer, Heavy Weight Compound
- BASF Ultramid® KR 4355 G7 35% Glass Filled PA6/6T (Dry)
Copyright © lookpolymers.com All Rights Reserved