Carpenter Gall-Tough PLUS™ Stainless, Annealed, 25% Cold Work

Category Metal , Ferrous Metal , Stainless Steel
Manufacturer Carpenter Technology Corporation (Cartech)
Trade Name Gall-Tough PLUS™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Carpenter Gall-Tough PLUS™ Stainless, Annealed, 25% Cold Work.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Data provided by Carpenter Technology Corporation.Annealed 1150°C, water quenched, and cold drawn.Threshold Galling Stress 48 MPa. The avg. total volume loss on the wear test is 10.6 mm³ at 100 rpm.Gall-Tough PLUS™ stainless is a high silicon, high manganese, nitrogen strengthened, austenitic stainless alloy which exhibits superior self-mated galling resistance and metal-to-metal wear resistance. The alloy possesses higher strength than Type 316. It also exhibits chloride corrosion resistance equal to or better then Type 316, along with equivalent high temperature oxidation resistance.Gall-Tough PLUS™ is a trademark of Carpenter Technology Corporation.
Physical Properties Metric English Comments
Density 7.60 g/cc
0.275 lb/in³
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 1027 MPa
149000 psi
1268 MPa

@Temperature -73.0 °C
183900 psi

@Temperature -99.4 °F
Tensile Strength, Yield 744 MPa

@Strain 0.200 %
108000 psi

@Strain 0.200 %
937 MPa

@Strain 0.200 %,
Temperature -73.0 °C
136000 psi

@Strain 0.200 %,
Temperature -99.4 °F
Elongation at Break 30 %
30 %
in 4D
31 %

@Temperature -73.0 °C
31 %

@Temperature -99.4 °F
in 4D
Reduction of Area 65 %
65 %
Modulus of Elasticity 184.9 GPa
26820 ksi
Thermal Properties Metric English Comments
CTE, linear 14.19 µm/m-°C

@Temperature 25.0 - 50.0 °C
7.883 µin/in-°F

@Temperature 77.0 - 122 °F
17.1 µm/m-°C

@Temperature 25.0 - 250 °C
9.48 µin/in-°F

@Temperature 77.0 - 482 °F
18.07 µm/m-°C

@Temperature 25.0 - 500 °C
10.04 µin/in-°F

@Temperature 77.0 - 932 °F
Specific Heat Capacity 0.5055 J/g-°C

@Temperature 50.0 - 100 °C
0.1208 BTU/lb-°F

@Temperature 122 - 212 °F
Thermal Conductivity 12.0 W/m-K
83.3 BTU-in/hr-ft²-°F
Maximum Service Temperature, Air 982 °C
1800 °F
Scaling Temperature for Continuous Service
Component Elements Properties Metric English Comments
Carbon, C <= 0.15 %
<= 0.15 %
Chromium, Cr 16.5 - 21 %
16.5 - 21 %
Iron, Fe 62 %
62 %
as remainder
Manganese, Mn 4.0 - 8.0 %
4.0 - 8.0 %
Molybdenum, Mo 0.50 - 2.5 %
0.50 - 2.5 %
Nickel, Ni 6.0 - 10 %
6.0 - 10 %
Nitrogen, N 0.050 - 0.35 %
0.050 - 0.35 %
Phosphorous, P <= 0.040 %
<= 0.040 %
Silicon, Si 2.5 - 4.5 %
2.5 - 4.5 %
Sulfur, S <= 0.040 %
<= 0.040 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.0000947 ohm-cm
0.0000947 ohm-cm