- Iran Petrochemical (PCC) 2602TH00 Low Density Polyethylene
Iran Petrochemical (PCC) 2602TH00 Low Density Polyethylene
| Category | Polymer , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade |
| Manufacturer | Iran Petrochemical Commercial Co. (PCC) |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Iran Petrochemical (PCC) 2602TH00 Low Density Polyethylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LDPE 2602TH00 high clarity film Applications: film, underblankets and films for medical applications.Information provided by Iran Petrochemical Commercial Co.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.926 g/cc | 0.0335 lb/in³ | ISO 1183 |
| Melt Flow | 1.9 g/10 min | 1.9 g/10 min | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 13.0 MPa | 1890 psi | ISO R527-1 |
| Film Tensile Strength at Yield, TD | 14.0 MPa | 2030 psi | ISO R527-1 |
| Film Elongation at Break, MD | >= 150 % | >= 150 % | ISO R527-1 |
| Film Elongation at Break, TD | >= 500 % | >= 500 % | ISO R527-1 |
| Modulus of Elasticity | 0.240 GPa | 34.8 ksi | MD; ISO R527-1 |
| 0.260 GPa | 37.7 ksi | TD; ISO R527-1 | |
| Tensile Impact | 150 J/cm | 281 ft-lb/in | ASTM D4272 |
| Coefficient of Friction | 1.0 | 1.0 | ASTM D1894 |
| Tear Strength | 40.0 kN/m | 228 pli | TD; ISO 6383-2 |
| 90.0 kN/m | 514 pli | MD; ISO 6383-2 | |
| Film Tensile Strength at Break, MD | 30.0 MPa | 4350 psi | ISO R527-1 |
| Film Tensile Strength at Break, TD | 20.0 MPa | 2900 psi | ISO R527-1 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 7.1 % | 7.1 % | ASTM D1003A |
| Gloss | 61 % | 61 % | ASTM D2457 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Clarity, mV | 11 | Sabtec |
Users viewing this material also viewed the following:
- LG Chemical Lutex M710 SBR Latex
- Lotus Nano Paint NAP 101 Nano-paint
- Saint-Gobain CHR® 2045-2 Skived PTFE Film Backing Silicone Adhesive Pressure Sensitive Tape
- Trelleborg R350 Natural Rubber Polyisoprene
- Ensinger TECASINT 3022 Polyimide, Black, 15% Graphite (PI)
- Teknor Apex APEX® 2590-H Polyvinyl Chloride, Flexible
- Toyobo E1080A Thermoplastic Polyurethane Elastomer, Extrusion Grade
- Materion Beryllium Copper Alloy 3 Wire; HT (TH04) Temper; 1.3-12.7 mm Diameter (UNS C17510)
- Polimeri Europa Extir Leonardo A 2000 AE Expandable Polystyrene (discontinued **)
Copyright © lookpolymers.com All Rights Reserved