Cadi 20 MOLD-MOR™

Category	Metal , Nonferrous Metal , Beryllium Alloy , Copper Alloy
Manufacturer	Cadi Company
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Cadi 20 MOLD-MOR™.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

A Beryllium Copper Alloy with high thermal conductivity and moderate hardness.Information provided by Cadi Company.

Physical Properties	Metric	English	Comments
Density	8.77 g/cc	0.317 lb/in³

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell B	98	98
Tensile Strength at Break	>= 607 MPa @Thickness >=50.8 mm	>= 88000 psi @Thickness >=2.00 in
	>= 621 MPa @Thickness 25.4 - 50.8 mm	>= 90000 psi @Thickness 1.00 - 2.00 in
	>= 648 MPa @Thickness <=25.4 mm	>= 94000 psi @Thickness <=1.00 in
Tensile Strength, Yield	>= 607 MPa @Strain 0.500 %, Thickness >=50.8 mm	>= 88000 psi @Strain 0.500 %, Thickness >=2.00 in
	>= 621 MPa @Strain 0.500 %, Thickness 25.4 - 50.8 mm	>= 90000 psi @Strain 0.500 %, Thickness 1.00 - 2.00 in
	>= 648 MPa @Strain 0.500 %, Thickness <=25.4 mm	>= 94000 psi @Strain 0.500 %, Thickness <=1.00 in
Modulus of Elasticity	131 GPa	19000 ksi
Poissons Ratio	0.267	0.267
Shear Modulus	51.7 GPa	7500 ksi

Thermal Properties	Metric	English	Comments
Thermal Conductivity	225 W/m-K	1560 BTU-in/hr-ft²-°F
Melting Point	1029 - 1068 °C	1885 - 1955 °F
Solidus	1029 °C	1885 °F
Liquidus	1068 °C	1955 °F

Component Elements Properties	Metric	English	Comments
Beryllium, Be	0.40 %	0.40 %
Copper, Cu	97.8 %	97.8 %
Nickel, Ni	1.8 %	1.8 %

Electrical Properties	Metric	English	Comments
Electrical Resistivity	<= 0.00000383 ohm-cm	<= 0.00000383 ohm-cm	Calculated from Min 45 %IACS, up to 3" diameter/any thickness

Processing Properties	Metric	English	Comments
Processing Temperature	788 °C	1450 °F	Brazing

Descriptive Properties	Value	Comments
RMWA Class	3