CLAL-MSX NICLAFOR® 1000 TF Quenched/Precipitation Heat Treated, Rolled Copper Alloy

Category	Metal , Nonferrous Metal , Copper Alloy
Manufacturer	CLAL-MSX
Trade Name	NICLAFOR®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	CLAL-MSX NICLAFOR® 1000 TF Quenched/Precipitation Heat Treated, Rolled Copper Alloy.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Finished parts can be produced with: reduction in sections, high mechanical properties even at high temperature, high spring properties, high conductivity, good resistance to corrosion, low permeability, good formability, long life duration. Meets environmental concern by not containing Beryllium, Cadmium nor Titanium.Applications:ElectrotechnicElectromechanicElectronicConnecticAutomotiveDomestic appliancesSpectacle industryTurned parts.Information provided by CLAL-MSX

Physical Properties	Metric	English	Comments
Density	8.90 g/cc	0.322 lb/in³

Mechanical Properties	Metric	English	Comments
Hardness, Vickers	230 - 270	230 - 270
Tensile Strength, Ultimate	740 - 860 MPa	107000 - 125000 psi
Tensile Strength, Yield	>= 510 MPa @Strain 0.200 %	>= 74000 psi @Strain 0.200 %
Elongation at Break	>= 10 %	>= 10 %	A<sub>50 mm</sub>
Modulus of Elasticity	120 GPa	17400 ksi
Modulus of Rigidity	50.0 GPa	7250 ksi	Torsion
Flexural Strength	566 MPa	82100 psi	Rigidty. Elastic bending fatigue, Longitudinal
	634 MPa	92000 psi	Rigidty. Elastic bending fatigue, Transverse
Fatigue Strength	450 MPa @# of Cycles 1.00e+7	65300 psi @# of Cycles 1.00e+7

Thermal Properties	Metric	English
CTE, linear	17.25 µm/m-°C @Temperature 20.0 - 200 °C	9.583 µin/in-°F @Temperature 68.0 - 392 °F
Thermal Conductivity	53.6 W/m-K	372 BTU-in/hr-ft²-°F
Melting Point	968 - 1078 °C	1770 - 1972 °F
Solidus	968 °C	1770 °F
Liquidus	1078 °C	1972 °F

Component Elements Properties	Metric	English
Copper, Cu	82.65 - 85.95 %	82.65 - 85.95 %
Iron, Fe	<= 0.50 %	<= 0.50 %
Lead, Pb	<= 0.030 %	<= 0.030 %
Manganese, Mn	0.050 - 0.30 %	0.050 - 0.30 %
Nickel, Ni	8.5 - 9.5 %	8.5 - 9.5 %
Phosphorous, P	<= 0.020 %	<= 0.020 %
Tin, Sn	5.5 - 6.5 %	5.5 - 6.5 %
Zinc, Zn	<= 0.50 %	<= 0.50 %

Electrical Properties	Metric	English	Comments
Electrical Resistivity	<= 0.00001433 ohm-cm	<= 0.00001433 ohm-cm	precipitation hardened (3h)
	<= 0.00001911 ohm-cm	<= 0.00001911 ohm-cm	quenched

Descriptive Properties	Value	Comments
Bending	0.5	90° bending across and in the rolling direction, longitudinal
	0.5	90° bending across and in the rolling direction, transverse