Braskem H 502 HC Injection Molding Polypropylene

Category	Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Molded
Manufacturer	Braskem
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Braskem H 502 HC Injection Molding Polypropylene.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: H 502HC is a low melt flow rate homopolymer, designed for very high stiffness/toughness applications with good processability. This product exhibits excellent chemical resitance and barrier properties. Applications: High stiffness parts; Household appliances; Disposable cups and plates; Hot fill packaging. Information provided by Braskem

Physical Properties	Metric	English	Comments
Density	0.905 g/cc	0.0327 lb/in³	ASTM D792A
Melt Flow	3.3 g/10 min @Load 2.16 kg, Temperature 230 °C	3.3 g/10 min @Load 4.76 lb, Temperature 446 °F	ASTM D1238L

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	110	110	ASTM D785
Tensile Strength, Yield	39.0 MPa	5660 psi	ASTM D638
Elongation at Yield	7.0 %	7.0 %	ASTM D638
Flexural Modulus	2.10 GPa	305 ksi	1% secant; ASTM D790
Izod Impact, Notched	0.200 J/cm @Temperature 23.0 °C	0.375 ft-lb/in @Temperature 73.4 °F	ASTM D256A

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	130 °C	266 °F	ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	68.0 °C	154 °F	ASTM D648
Vicat Softening Point	160 °C	320 °F	10 N; ASTM D1525