Braskem CN8092 EVA Molding Copolymer

Category	Polymer , Thermoplastic , Ethylene Vinyl Acetate
Manufacturer	Braskem
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Braskem CN8092 EVA Molding Copolymer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

CN8092 is an Ethylene-Vinyl Acetate copolymer (EVA) which has a molecular structure that provides easy processing, adhesion, resilience, low hardness, good moisture, and gas barrier properties. It is a non-halogen resin that has excellent thermal stability and a low content of oligomers, with low influence on organoleptic properties of the products. The melt properties of this resin allow processability in cast film and tubular film equipment. It contains antioxidant additives. Its applications include: base resin for production of compounds for cap liners in carbonated beverages; compounds; and master batches.

Physical Properties	Metric	English	Comments
Density	0.934 g/cc	0.0337 lb/in³	ASTM-D1505
Vinyl Acetate Content	15.5 %	15.5 %
Melt Flow	8.5 g/10 min @Load 2.16 kg, Temperature 190 °C	8.5 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM-D1238

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	91	91	ASTM-D2240
Hardness, Shore D	44	44	ASTM-D2240
Tensile Strength at Break	17.0 MPa	2470 psi	ASTM-D638
Tensile Strength, Yield	4.70 MPa	682 psi	ASTM-D638
Elongation at Break	720 %	720 %	ASTM-D638
1% Secant Modulus	72.0 MPa	10400 psi	ASTM-D638

Thermal Properties	Metric	English	Comments
Melting Point	90.0 °C	194 °F	ASTM-D3418
Vicat Softening Point	62.0 °C @Load 1.02 kg	144 °F @Load 2.25 lb	ASTM-D1525

Processing Properties	Metric	English	Comments
Melt Temperature	135 - 150 °C	275 - 302 °F	Blow Film Extrusion
	205 - 210 °C	401 - 410 °F	Cast Film Extrusion
	225 °C	437 °F	Extrusion Coating
Die Opening	0.0800 - 0.100 cm	0.0315 - 0.0394 in	Blow Film Extrusion
Blow-up Ratio (BUR)	2.0 - 3.0	2.0 - 3.0	Blow Film Extrusion
Roll Temperature	25.0 °C	77.0 °F	Chill, Cast Film Extrusion