Borealis RA130E-2491 Polypropylene Random Copolymer

Category	Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene Copolymer
Manufacturer	Borealis
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Borealis RA130E-2491 Polypropylene Random Copolymer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

RA130E-2491 is a high molecular weight, low melt flow rate polypropylene random copolymer (PP-R) compound and is blue colored. Applications: domestic water, heating, relining, plumbing, and industrial applications. The product is used for single as well as for multilayer pipes, where you then differentiate between plastic multilayer and aluminum multilayer pipes. Specifications: DIN 8078; DIN 8077; and EN ISO 15874.Information provided by Borealis AG

Physical Properties	Metric	English	Comments
Density	0.905 g/cc	0.0327 lb/in³	ISO 1183
Melt Flow	0.30 g/10 min @Load 2.16 kg, Temperature 230 °C	0.30 g/10 min @Load 4.76 lb, Temperature 446 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	25.0 MPa	3630 psi	50mm/min; ISO 527-2
Elongation at Yield	13.5 %	13.5 %	50mm/min; ISO 527-2
Tensile Modulus	0.900 GPa	131 ksi	1mm/min; ISO 527
Flexural Modulus	0.800 GPa	116 ksi	2mm/min; ISO 178
Charpy Impact Unnotched	4.00 J/cm² @Temperature -20.0 °C	19.0 ft-lb/in² @Temperature -4.00 °F	ISO 179/1eU
	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F	ISO 179/1eU
	NB @Temperature 0.000 °C	NB @Temperature 32.0 °F	ISO 179/1eU
Charpy Impact, Notched	0.200 J/cm² @Temperature -20.0 °C	0.952 ft-lb/in² @Temperature -4.00 °F	ISO 179/1eA
	0.350 J/cm² @Temperature 0.000 °C	1.67 ft-lb/in² @Temperature 32.0 °F	ISO 179/1eA
	2.00 J/cm² @Temperature 23.0 °C	9.52 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eA

Thermal Properties	Metric	English	Comments
CTE, linear	150 µm/m-°C @Temperature 0.000 - 70.0 °C	83.3 µin/in-°F @Temperature 32.0 - 158 °F	DIN 53752
Thermal Conductivity	0.240 W/m-K	1.67 BTU-in/hr-ft²-°F	DIN 52612

Processing Properties	Metric	English	Comments
Middle Barrel Temperature	180 - 210 °C	356 - 410 °F	cylinder
Die Temperature	210 - 220 °C	410 - 428 °F
Melt Temperature	210 - 220 °C	410 - 428 °F
Head Temperature	210 - 220 °C	410 - 428 °F