Borealis Daplen™ EG103AI Polypropylene Compound, Mineral Filled

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Mica Filler
Manufacturer Borealis
Trade Name Daplen™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Borealis Daplen™ EG103AI Polypropylene Compound, Mineral Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Daplen™ EG103AI is a 15 % mineral filled polypropylene compound intended for injection molding. This material has an excellent balance between impact strength and stiffness and high melt flow rate. Applications: Daplen™ EG103AI has been developed especially for the automotive industry including door panels and pockets, and other automotive interior parts.Information provided by Borealis AG
Physical Properties Metric English Comments
Density 1.02 g/cc
0.0368 lb/in³
ISO 1183
Linear Mold Shrinkage 0.0090 cm/cm
0.0090 in/in
mold average;Borealis Method
Melt Flow 26 g/10 min

@Load 2.16 kg,
Temperature 230 °C
26 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ISO 1133
Mechanical Properties Metric English Comments
Ball Indentation Hardness 49.0 MPa
7110 psi
H 358/30
Tensile Strength, Yield 22.0 MPa
3190 psi
50mm/min; ISO 527-2
Elongation at Yield 5.0 %
5.0 %
50mm/min; ISO 527-2
Tensile Modulus 1.80 GPa
261 ksi
1mm/min; ISO 527-2
Flexural Modulus 1.90 GPa
276 ksi
2mm/min; ISO 178
Charpy Impact Unnotched 6.00 J/cm²

@Temperature -20.0 °C
28.6 ft-lb/in²

@Temperature -4.00 °F
ISO 179/1eU
15.0 J/cm²

@Temperature 23.0 °C
71.4 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched 0.300 J/cm²

@Temperature -20.0 °C
1.43 ft-lb/in²

@Temperature -4.00 °F
ISO 179/1eA
1.50 J/cm²

@Temperature 23.0 °C
7.14 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 105 °C
221 °F
ISO 75-2
Deflection Temperature at 1.8 MPa (264 psi) 54.0 °C
129 °F
ISO 75-2
Vicat Softening Point 54.0 °C

@Load 5.10 kg
129 °F

@Load 11.2 lb
ISO 306
140 °C

@Load 1.02 kg
284 °F

@Load 2.25 lb
ISO 306
Processing Properties Metric English Comments
Processing Temperature 220 - 260 °C
428 - 500 °F
mass temperature
Mold Temperature 30.0 - 50.0 °C
86.0 - 122 °F
Injection Velocity 100 - 200 mm/sec
3.94 - 7.87 in/sec
Hold Pressure 3.00 - 6.00 MPa
435 - 870 psi
Descriptive Properties Value Comments
Emission (µgC/g) < 60
VDA 277
Fogging (mg) < 2
DIN 75201;100°C, 16h
Screw Speed low to medium