Borealis Borstar® HE6067 Black Bimodal HD Polyethylene Compound for Jacketing of Communication and Power Cables

Category Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Extruded
Manufacturer Borealis
Trade Name Borstar®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Borealis Borstar® HE6067 Black Bimodal HD Polyethylene Compound for Jacketing of Communication and Power Cables.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Borstar HE6067 is a black, bimodal, co-polymer high density polyethylene (HDPE) compound produced according to the bimodal Borstar process. It is characterized by its balanced properties important in jacketing applications. For example, very low shrink-back, excellent stress-crack resistance and a wide processing window. HE6067 can resist severe laying condition even at elevated temperature. Processing conditions however, must be optimized for best surface conditions whenever jacketing large diameter cables. Borstar HE6067 is especially well suited for fiber optic applications due to its very low shrinkage back characteristics as well as power cable jacketing.Information provided by the Manufacturer.
Physical Properties Metric English Comments
Density 0.942 g/cc
0.0340 lb/in³
Base; ASTM D792
0.954 g/cc
0.0345 lb/in³
Compound; ASTM D792
ESCR 10% Igepal® >= 2000 hour

@Temperature 50.0 °C
>= 2000 hour

@Temperature 122 °F
ASTM D1693/B
Melt Flow 1.7 g/10 min
1.7 g/10 min
ASTM D1238/E
Mechanical Properties Metric English Comments
Hardness, Shore D 61
61
ASTM D2240
Tensile Strength at Break 25.0 MPa
3630 psi
ASTM D638
Tensile Strength, Yield 13.8 MPa
2000 psi
ASTM D638
Elongation at Break 700 %
700 %
ASTM D638
Flexural Modulus 0.850 GPa
123 ksi
ASTM D790/1
Thermal Properties Metric English Comments
Brittleness Temperature <= -76.0 °C
<= -105 °F
ASTM D746
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+16 ohm-cm
1.00e+16 ohm-cm
ASTM D257
Dielectric Strength >= 19.7 kV/mm
>= 500 kV/in
At 50 mils; ASTM D149
Processing Properties Metric English Comments
Middle Barrel Temperature >= 210 °C
>= 410 °F
Front Barrel Temperature >= 160 °C
>= 320 °F
Head Temperature >= 210 °C
>= 410 °F