Borealis Borcoat™ BB127E Polypropylene Adhesive Powder form for Steel Pipe Coating

Category	Polymer , Thermoplastic , Polypropylene (PP)
Manufacturer	Borealis
Trade Name	Borcoat™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Borealis Borcoat™ BB127E Polypropylene Adhesive Powder form for Steel Pipe Coating.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Borcoat BB127E is a chemically modified polypropylene copolymer designed to be used as the tie layer between the epoxy corrosion protection layer and the Top-coat polypropylene coating Borcoat BB108E-1199.Borcoat BB127E is delivered in powder form and can be applied with an ordinary epoxy powder gun. It has excellent adhesion to fusion bonded epoxy and polypropylene. Furthermore it has superior thermal properties and can be used at operating temperatures within the range of -10°C to 110°C, and up to 140°C for specific offshore projects.Information provided by the Manufacturer.

Physical Properties	Metric	English	Comments
Density	0.900 g/cc	0.0325 lb/in³	ISO 1183
Melt Flow	8.0 g/10 min @Load 2.16 kg, Temperature 230 °C	8.0 g/10 min @Load 4.76 lb, Temperature 446 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	58	58	ISO 868
Tensile Strength, Yield	22.0 MPa	3190 psi	At 50 mm/min; ISO 527-2
Elongation at Yield	6.0 %	6.0 %	At 50 mm/min; ISO 527-2
Tensile Modulus	1.10 GPa	160 ksi	At 1 mm/min; ISO 527-2
Izod Impact, Notched (ISO)	15.0 kJ/m²	7.14 ft-lb/in²	ISO 108/1A
Peel Strength	>= 3.00 kN/m	>= 17.1 pli	3-layer at 140°C; DIN 30678
	>= 4.00 kN/m	>= 22.8 pli	3-layer at 110°C; DIN 30678
	>= 10.0 kN/m	>= 57.1 pli	3-layer at 80°C; DIN 30678
	>= 20.0 kN/m	>= 114 pli	3-layer; DIN 30678

Thermal Properties	Metric	English	Comments
Vicat Softening Point	145 °C	293 °F	A50 (10 N); ISO 306

Processing Properties	Metric	English	Comments
Front Barrel Temperature	235 - 245 °C	455 - 473 °F
Head Temperature	235 - 245 °C	455 - 473 °F