Bond Laminates TEPEX® dynalite 208-C200(x)/45% Carbon - TPU Consolidated Composite Laminate

Category	Polymer , Thermoplastic , Polyurethane, TP , Thermoplastic Polyurethane (TPUR), Carbon Fiber Reinforced
Manufacturer	Bond Laminates
Trade Name	TEPEX® dynalite
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Bond Laminates TEPEX® dynalite 208-C200(x)/45% Carbon - TPU Consolidated Composite Laminate.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Within the TEPEX® composite laminate, TPU distinguishes itself from alternative resin systems by its specific physical properties. The TPU resin is tough which results in an excellent impact and easy to mold, obtaining an excellent surface quality. The TPU-glass laminates can easily be bonded with common adhesive systems. An excellent adhesion is achieved when over molding with injection molding TPU grades.Typical application environments are sporting goods applications, helmet shells, cosmetic applications, footwearInformation provided by Bond Laminates, GmbH.

Physical Properties	Metric	English	Comments
Density	1.47 g/cc	0.0531 lb/in³
Filler Content	45 %	45 %	by volume
Thickness	250 microns	9.84 mil	laminate layer thickness

Mechanical Properties	Metric	English	Comments
Tensile Strength	705 MPa	102000 psi	transverse; ISO 527-4/5
	710 MPa	103000 psi	longitudinal; ISO 527-4/5
Elongation at Break	1.5 %	1.5 %	longitudinal; ISO 527-4/5
	1.5 %	1.5 %	transverse; ISO 527-4/5
Tensile Modulus	48.0 GPa	6960 ksi	transverse; ISO 527-4/5
	48.5 GPa	7030 ksi	longitudinal; ISO 527-4/5
Flexural Strength	735 MPa	107000 psi	transverse; ISO 178
	745 MPa	108000 psi	longitudinal; ISO 178
Flexural Modulus	41.5 GPa	6020 ksi	transverse; ISO 178
	42.5 GPa	6160 ksi	longitudinal; ISO 178

Thermal Properties	Metric	English	Comments
Melting Point	190 °C	374 °F	DSC 3146
Maximum Service Temperature, Air	90.0 °C @Time 7.20e+7 sec	194 °F @Time 20000 hour	Relative Temperature Index; IEC 216/1
Deflection Temperature at 1.8 MPa (264 psi)	185 °C	365 °F	ISO 75-1/2
Minimum Service Temperature, Air	-30.0 °C	-22.0 °F

Processing Properties	Metric	English	Comments
Processing Temperature	210 - 230 °C	410 - 446 °F

Descriptive Properties	Value	Comments
Reinforcement	Area weight	200 g/m²
	Fabric	twill 2/2
	Fibers	carbon
	Weight Rate	50% longitudinal and transverse
	Yarn	3000 tex longitudinal and transverse