BiologiQ EcoStarch GS270 Thermoplastic Starch

Category Polymer , Renewable/Recycled Polymer , Thermoplastic
Manufacturer BiologiQ
Trade Name EcoStarch
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BiologiQ EcoStarch GS270 Thermoplastic Starch.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
BiologiQ GS270 is a plasticized thermoplastic starch (TPS) called EcoStarch Resin (ESR). It is suitable for blending with petrochemical or bioresins where biobased content is desired. It Can be used as a stand alone polymer for certain low-temperature injection molding applications. It is highly compostable and biodegradable. It forms a crystalline structure product that has good strength and low plasticity. When GS270 absorbs moisture it exhibits plastic behavior and becomes flexible. When removed from humidity the material dries out and becomes crystalline again. Used for final products requiring plasticity such as plastic dinnerware, packaging. Blend with PE to make think film products like shopping bags.Information provided by BiologiQ
Physical Properties Metric English Comments
Density 1.40 g/cc
0.0506 lb/in³
ASTM D792
Melt Flow 1.98 g/10 min

@Load 5.00 kg,
Temperature 200 °C
1.98 g/10 min

@Load 11.0 lb,
Temperature 392 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break >= 30.0 MPa
>= 4350 psi
ASTM D638
Tensile Strength, Yield >= 30.0 MPa
>= 4350 psi
ASTM D638
Elongation at Break <= 10 %
<= 10 %
ASTM D638
Tensile Modulus 1.50 GPa
218 ksi
ASTM D638
Dart Drop Test 3500 g
7.72 lb
ASTM D5628
Thermal Properties Metric English Comments
Melting Point 166 - 180 °C
331 - 356 °F
ASTM D3418
Glass Transition Temp, Tg 81.0 - 100 °C
178 - 212 °F
ASTM D3418
Processing Properties Metric English Comments
Drying Temperature 60.0 °C
140 °F
Dry Time 1.00 - 4.00 hour
1.00 - 4.00 hour
Moisture Content <= 1.0 %
<= 1.0 %
ASTM D6980