PolyOne Stat-Tech™ PI-05CF/000 Polyetherimide - 5% Carbon Fibers - ESD Applications (discontinued **)
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) , Polyetherimide (PEI), Carbon Fiber Filled |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Stat-Tech™ PI-05CF/000 Polyetherimide - 5% Carbon Fibers - ESD Applications
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by PolyOne.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.29 g/cc | 0.0466 lb/in³ | ASTM D792 |
| Water Absorption | 0.25 % | 0.25 % | 24 hrs. ASTM D570 |
| Linear Mold Shrinkage | 0.0040 cm/cm @Thickness 3.17 mm |
0.0040 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 109 | 109 | ASTM D785 |
| Tensile Strength, Ultimate | 124 MPa | 18000 psi | ASTM D638 |
| Elongation at Break | 4.0 - 5.0 % | 4.0 - 5.0 % | ASTM D638 |
| Tensile Modulus | 4.50 GPa | 653 ksi | ASTM D638 |
| Flexural Yield Strength | 193 MPa | 28000 psi | ASTM D790 |
| Flexural Modulus | 4.50 GPa | 653 ksi | ASTM D790 |
| Izod Impact, Notched | 0.460 J/cm @Thickness 6.35 mm |
0.862 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 207 °C | 405 °F | ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | >= 1e+6 ohm-cm | >= 1e+6 ohm-cm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 354 - 382 °C | 669 - 720 °F | Stock |
| Mold Temperature | 121 °C | 250 °F | |
| Drying Temperature | 135 °C | 275 °F |
Users viewing this material also viewed the following:
- Haynes Ultimet® alloy, aged 1000 hours at 871°C (1600°F)
- Unifrax Foamfrax® HD Grade II Fiber HD Insulation
- A. Schulman POLYBATCH™ Silver Metallic 70153 Concentrate Based In LDPE
- Eifeler Coatings Technology TiN PVD Coating
- Covestro Makrolon® 2256 Polycarbonate
- Eurotec® Tecotek® BC40 UF45 NL CE PC/ABS, unfilled, heat & UV stabilized, natural, easy flow grade
- Asahi Kasei Thermofil P-20CC-0734A 20% Calcium Carbonate Reinforced
- Polykemi AB POLYfill PPH TS15030 Polypropylene Homopolymer, Mineral Reinforced
- Ineos ABS Triax® KU2-3154 ABS + Polyamide Blend (DAM), Injection Molding Grade
Copyright © lookpolymers.com All Rights Reserved