Bhansali Engineering Abstron MIF-45 ABS Injection Molding Grade

Category Polymer , Thermoplastic , ABS Polymer
Manufacturer Bhansali Engineering
Trade Name Abstron
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Bhansali Engineering Abstron MIF-45 ABS Injection Molding Grade.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
High Impact, Medium, High Flow, General PurposeInformation provided by Bhansali
Physical Properties Metric English Comments
Density 1.045 g/cc
0.03775 lb/in³
ASTM D-792
Linear Mold Shrinkage 0.0040 - 0.0060 cm/cm
0.0040 - 0.0060 in/in
ASTM D-955
Melt Flow 43 g/10 min

@Load 10.0 kg,
Temperature 220 °C
 43 g/10 min

@Load 22.0 lb,
Temperature 428 °F
 ASTM D-1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 110
110
ASTM D-785
Tensile Strength, Yield 41.2 MPa

@Thickness 3.20 mm
 5970 psi

@Thickness 0.126 in
 Type 1; ASTM D638
Flexural Yield Strength 63.7 MPa

@Thickness 6.40 mm
 9250 psi

@Thickness 0.252 in
 ASTM D790
Flexural Modulus 2.21 GPa

@Thickness 6.40 mm
 320 ksi

@Thickness 0.252 in
 ASTM D790
Izod Impact, Notched 2.16 J/cm

@Thickness 6.40 mm
 4.04 ft-lb/in

@Thickness 0.252 in
 ASTM D256
2.7451 J/cm

@Thickness 3.20 mm
 5.1427 ft-lb/in

@Thickness 0.126 in
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 93.0 °C
199 °F
Method A - Annealed; ASTM D-648
Vicat Softening Point 103 °C
217 °F
Method B; ASTM D-1525
Flammability, UL94 HB

@Thickness 3.20 mm
 HB

@Thickness 0.126 in
 UL-94