Bhansali Engineering Abstron IMC-45 ABS-PC Alloy

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer Bhansali Engineering
Trade Name Abstron
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Bhansali Engineering Abstron IMC-45 ABS-PC Alloy.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
ABS-polycarbonate alloys for High service temperature applications.Information provided by Bhansali
Physical Properties Metric English Comments
Density 1.12 g/cc
0.0405 lb/in³
ASTM D-792
Linear Mold Shrinkage 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
ASTM D-955
Melt Flow 13 g/10 min

@Load 10.0 kg,
Temperature 220 °C
 13 g/10 min

@Load 22.0 lb,
Temperature 428 °F
 ASTM D-1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 112
112
ASTM D-785
Tensile Strength, Yield 51.98 MPa

@Thickness 3.20 mm
 7538 psi

@Thickness 0.126 in
 Type 1, 5 mm/min; ASTM D-638
Flexural Yield Strength 78.5 MPa

@Thickness 6.40 mm
 11400 psi

@Thickness 0.252 in
 ASTM D-790
Flexural Modulus 2.21 GPa

@Thickness 6.40 mm
 320 ksi

@Thickness 0.252 in
 ASTM D-790
Izod Impact, Notched 3.92 J/cm

@Thickness 6.40 mm
 7.35 ft-lb/in

@Thickness 0.252 in
 ASTM D-256
5.49 J/cm

@Thickness 3.20 mm
 10.3 ft-lb/in

@Thickness 0.126 in
 ASTM D-256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 105 °C
221 °F
Method A - Annealed; ASTM D-648
Vicat Softening Point 115 °C
239 °F
Method B; ASTM D-1525
Flammability, UL94 HB

@Thickness 3.20 mm
 HB

@Thickness 0.126 in
 UL-94