Bhansali Engineering Abstron IM21M ABS Injection Molding Grade

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded
Manufacturer Bhansali Engineering
Trade Name Abstron
Port Shanghai port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF Bhansali Engineering Abstron IM21M ABS Injection Molding Grade.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Medium Flow, Medium Impact, Medium RigidityInformation provided by Bhansali
Physical Properties Metric English Comments
Specific Gravity 1.045 g/cc
1.045 g/cc
ASTM D792
Linear Mold Shrinkage 0.00400 - 0.00600 cm/cm
0.00400 - 0.00600 in/in
ASTM D955
Melt Flow 32.0 g/10 min
<br>@Load 10.0 kg,<br> Temperature 220 °C
 32.0 g/10 min
<br>@Load 22.0 lb,<br> Temperature 428 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 113
113
ASTM D785
Tensile Strength, Yield 48.1 MPa
<br>@Thickness 3.20 mm
 6970 psi
<br>@Thickness 0.126 in
 Type I, 5 mm/min; ASTM D638
Flexural Yield Strength 70.6 MPa
<br>@Thickness 6.40 mm
 10200 psi
<br>@Thickness 0.252 in
 5 mm/min; ASTM D790
Flexural Modulus 2.35 GPa
<br>@Thickness 6.40 mm
 341 ksi
<br>@Thickness 0.252 in
 5 mm/min; ASTM D790
Izod Impact, Notched 1.67 J/cm
<br>@Thickness 6.40 mm
 3.12 ft-lb/in
<br>@Thickness 0.252 in
 ASTM D256
2.06 J/cm
<br>@Thickness 3.20 mm
 3.86 ft-lb/in
<br>@Thickness 0.126 in
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 95.0 °C
<br>@Thickness 6.40 mm
 203 °F
<br>@Thickness 0.252 in
 Method A; ASTM D648
Flammability, UL94 HB
<br>@Thickness 3.20 mm
 HB
<br>@Thickness 0.126 in