Beijing Chemical Industry KAIFA® 304-GO0 PBT Resin
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Flame Retardant |
| Manufacturer | Beijing Chemical Industry Research Institute (Group) |
| Trade Name | KAIFA® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Beijing Chemical Industry KAIFA® 304-GO0 PBT Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Flame retardant, low bleeding, UV-resistantInformation provided by Beijing Chemical Industry Research Institute (Group)
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.60 g/cc | 0.0578 lb/in³ | ASTM D792 |
| Water Absorption | 0.070 % | 0.070 % | 24 hr; ASTM D570 |
| Linear Mold Shrinkage | 0.0040 - 0.0080 cm/cm | 0.0040 - 0.0080 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 50.0 MPa | 7250 psi | ASTM D638 |
| Flexural Strength | 90.0 MPa | 13100 psi | ASTM D790 |
| Flexural Modulus | 2.20 GPa | 319 ksi | ASTM D790 |
| Izod Impact, Notched | 0.300 J/cm @Thickness 3.20 mm |
0.562 ft-lb/in @Thickness 0.126 in |
ASTM D256 |
| Charpy Impact Unnotched | 3.50 J/cm² | 16.7 ft-lb/in² | ISO179 |
| Charpy Impact, Notched | 0.400 J/cm² | 1.90 ft-lb/in² | ISO179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 70.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
38.9 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 3.20 mm |
V-0 @Thickness 0.126 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.0 @Frequency 1e+6 Hz |
3.0 @Frequency 1e+6 Hz |
ASTM D150 |
| Dielectric Strength | 21.0 kV/mm @Thickness 2.00 mm |
533 kV/in @Thickness 0.0787 in |
ASTM D149 |
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz |
0.020 @Frequency 1e+6 Hz |
ASTM D150 |
Users viewing this material also viewed the following:
- PolyOne Therma-Tech™ SF-4500 TC Polyphenylene Sulfide (PPS)
- SABIC Innovative Plastics GELOY HRA222F ASA+PC (Europe-Africa-Middle East)
- DuPont™ Clysar® EHC Polyolefin Shrink Packaging Film, 100 Gauge (discontinued **)
- Mid-Mountain Materials THERMOSEAL® A Rigidizer
- Eurostar Staramide BG6ST43 PA6, 30% Glass Fiber Filled, Impact Modified, Injection Molded
- DSM Novamid® MC112LG55 C10 PA6-GF55
Copyright © lookpolymers.com All Rights Reserved