- Barlog Plastics KEBATER B510 PBT unreinforced
Barlog Plastics KEBATER B510 PBT unreinforced
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Unreinforced, Molded |
| Manufacturer | Barlog Plastics |
| Trade Name | KEBATER |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Barlog Plastics KEBATER B510 PBT unreinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PBTInformation provided by BARLOG plastics GmbH.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.29 g/cc | 0.0466 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | similar to ISO 62 test |
| Melt Flow | 20 g/10 min @Load 2.16 kg, Temperature 235 °C |
20 g/10 min @Load 4.76 lb, Temperature 455 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 58.0 MPa | 8410 psi | ISO 527-1 |
| Elongation at Break | >= 25 % | >= 25 % | ISO 527-1 |
| Elongation at Yield | 3.5 % | 3.5 % | ISO 527-1 |
| Tensile Modulus | 2.50 GPa | 363 ksi | ISO 527-1 |
| Charpy Impact Unnotched | NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
ISO 179-1eU |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179-1eU | |
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | ISO 179-1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 225 °C | 437 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 155 °C | 311 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ISO 75-1/-2 |
| Flammability, UL94 | HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
IEC 60695-11-10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Resin Type | PBT |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® 3413HF PC
- IDI Composites M-209 Thermoset Polyester, Sheet
- Karina E 854-18/99-CRB Gray PVC Compound
- SABIC Innovative Plastics LNP LUBRILOY DF202P PC
- Tra-Con Tra-Bond 216E02 Encapsulant for "Fill" Applications
- Domo 1040N Polypropylene Homopolymer
- Azoty Tarnow™ TARFLEN SM-K25 PTFE
Copyright © lookpolymers.com All Rights Reserved