Quantum Polycarbonate 20% Glass Fiber Filled
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 20% Glass Filled |
| Manufacturer | Quantum Advanced Engineering Plastics |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Quantum Polycarbonate 20% Glass Fiber Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Quantum Advanced Engineering Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.35 g/cc | 1.35 g/cc | ASTM D792 |
| Water Absorption | 0.16 % | 0.16 % | ASTM D570 |
| Water Absorption at Saturation | 0.29 % | 0.29 % | ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 91 | 91 | ASTM D785 |
| Hardness, Rockwell R | 122 | 122 | ASTM D785 |
| Hardness, Shore D | 80 | 80 | ASTM 2240 |
| Tensile Strength | 110 MPa | 16000 psi | ASTM D638 |
| Elongation at Break | 5.0 % | 5.0 % | ASTM D638 |
| Tensile Modulus | 5.93 GPa | 860 ksi | ASTM D638 |
| Flexural Strength | 131 MPa | 19000 psi | ASTM D790 |
| Flexural Modulus | 5.52 GPa | 800 ksi | ASTM D790 |
| Compressive Strength | 110 MPa | 16000 psi | ASTM D695 |
| Izod Impact, Notched | 1.07 J/cm | 2.00 ft-lb/in | ASTM D256 |
| Coefficient of Friction | 0.22 | 0.22 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 27.0 µm/m-°C | 15.0 µin/in-°F | ASTM D696 |
| Thermal Conductivity | 0.212 W/m-K | 1.47 BTU-in/hr-ft²-°F | ASTM C177 |
| Melting Point | 166 °C | 330 °F | ASTM D3417 |
| Maximum Service Temperature, Air | 127 °C | 260 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 149 °C | 300 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 146 °C | 295 °F | ASTM D648 |
| Flammability, UL94 | V-1 | V-1 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+17 ohm-cm | 1.00e+17 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.13 @Frequency 1.00e+6 Hz |
3.13 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Dielectric Strength | 19.3 kV/mm | 490 kV/in | ASTM D149 |
| Dissipation Factor | 0.0090 @Frequency 1.00e+6 Hz |
0.0090 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| FDA Compliance | no |
Users viewing this material also viewed the following:
- RheTech Products HP514-438 14% Talc Reinforced High Performance Polypropylene Copolymer, UV Stabilized, 167 Ebony
- Precision Polymer Engineering V75B Fluoroelastomer Compound
- Fainplast Compounds RST 171 Rigid PVC, Extrusion Lead Free
- Lucite International Elvacite ® 2927 Acrylic Resin
- Lehmann & Voss LUVOCOM® 1301-7629/EG PPS, linear, with carbon fiber
- Mearthane Durethaneâ„¢ S DS-240A Solid Polyurethane Elastomer
- DuPont™ Surlyn® 8140 Ionomer Resin, Sodium
- Dow Corning 5329 Modifier
- Asahi Glass AFLAS® 100S TFE/P Fluoroelastomer
- 3M Scotch® 610 Cellophane Film Tape
Copyright © lookpolymers.com All Rights Reserved