BNZ Materials Zelieblok 2000S Structural Ceramic Insulation
| Category | Ceramic , Oxide , Silicon Oxide |
| Manufacturer | BNZ Materials, Inc. |
| Trade Name | Zelieblok |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BNZ Materials Zelieblok 2000S Structural Ceramic Insulation.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by BNZ Materials Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.260 g/cc | 0.00937 lb/in³ | |
| Density | 0.705 g/cc | 0.0255 lb/in³ | ASTM C134 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Rupture | 0.00120 GPa | 0.174 ksi | ASTM C133 |
| Compressive Strength | 1.60 MPa | 232 psi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 6.00 µm/m-°C @Temperature 20.0 - 1093 °C |
3.33 µin/in-°F @Temperature 68.0 - 1999 °F |
|
| Thermal Conductivity | 0.0700 W/m-K @Temperature 200 °C |
0.486 BTU-in/hr-ft²-°F @Temperature 392 °F |
ASTM C182 |
| 0.0900 W/m-K @Temperature 400 °C |
0.625 BTU-in/hr-ft²-°F @Temperature 752 °F |
ASTM C182 | |
| 0.100 W/m-K @Temperature 600 °C |
0.694 BTU-in/hr-ft²-°F @Temperature 1110 °F |
ASTM C182 | |
| Maximum Service Temperature, Air | 1100 °C | 2010 °F | |
| Shrinkage | 1.00 % @Temperature 1050 °C, Time 43200 sec |
1.00 % @Temperature 1920 °F, Time 12.0 hour |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Al2O3 | 0.30 % | 0.30 % | |
| CaO | 45 % | 45 % | |
| Fe2O3 | 0.30 % | 0.30 % | |
| K2O | 0.10 % | 0.10 % | |
| Loss on Ignition(%) | 6.0 % | 6.0 % | |
| MgO | 0.60 % | 0.60 % | |
| SiO2 | 47 % | 47 % | |
| TiO2 | 0.10 % | 0.10 % |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Flexible XV3437 Polyvinyl Chloride, Flexible (PVC, Flexible)
- Lanxess Durethan® BC 40 SR2 000000 Nylon 6
- A. Schulman POLYBLAK™ 3225 Superior Black Color Concentrate, 50% Carbon Black Based In PP Homopolymer
- Eastman Tenite 307E0V16310 Propionate Clear, Trsp
- Ecomass® 1850ZD96 Tungsten Filled Polyamide
- Dow VORANOL™ VORACTIV™ 6340 Catalytically Active Polyether Polyol
- Addcomp ADD-MAX® 104 Efficiency masterbatch, LDPE based
- 3M Scotch-Weld™ 1838 B/A Tan Two-Part Structural Adhesive
- Rogers Corporation 2929 Bondply Unreinforced, Hydrocarbon based Thin Film Adhesive System
Copyright © lookpolymers.com All Rights Reserved