- BLUESTAR 403G-MG20 PBT, 20% Glass Filled
BLUESTAR 403G-MG20 PBT, 20% Glass Filled
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 20% Glass Fiber Filled |
| Manufacturer | BLUESTAR |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BLUESTAR 403G-MG20 PBT, 20% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Typical Applications: High GWIT, RTI, E/EInformation provided by Polymer Technology and Services, LLC (PTS).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.56 g/cc | 1.56 g/cc | ASTM D792 |
| Moisture Absorption at Equilibrium | 0.17 % | 0.17 % | 50% RH; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm | 0.0040 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm | 0.0070 in/in | ASTM D955 |
| Melt Flow | 25 g/10 min @Load 2.16 kg, Temperature 250 °C |
25 g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 100 MPa | 14500 psi | ASTM D638 |
| Elongation at Break | 3.5 % | 3.5 % | ASTM D638 |
| Tensile Modulus | 7.00 GPa | 1020 ksi | ASTM D638 |
| Flexural Strength | 170 MPa | 24700 psi | ASTM D790 |
| Flexural Modulus | 6.00 GPa | 870 ksi | ASTM D790 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | ASTM D256 |
| Izod Impact, Unnotched (ISO) | 60.0 kJ/m² | 28.6 ft-lb/in² | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 219 °C | 426 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 204 °C | 399 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
|
| V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
||
| V-0 @Thickness 3.20 mm |
V-0 @Thickness 0.126 in |
||
| Glow Wire Test | 750 °C | 1380 °F | GWIT |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.20e+16 ohm-cm | 1.20e+16 ohm-cm | ASTM D257 |
| Dielectric Strength | 20.0 kV/mm | 508 kV/in | ASTM D149 |
Users viewing this material also viewed the following:
- Park Electrochemical Nelcote® F-555 Phenolic Prepreg, NARC/CYDSA Reinforced
- SABIC Innovative Plastics Lexan® 101 PC (Europe-Africa-Middle East)
- Solvay Specialty Polymers Primef® 7010 Polyphenylene Sulfide (PPS), 65% GlassMineral (discontinued **)
- Huntsman Araldite GZ 571 T-75 Bisphenol A Epoxy Solution
- Dow BETAMATE™ 7050 L Epoxy
- Arlon 44562R011 0.011" Cured Silicone Rubber with Fiberglass
- Polymer Resources PPX-G10 Modified PPO, 10% Glass Reinforced (Unverified Data**)
- DuPont Performance Polymers Hypalon® 20 Chlorosulfonated Polyethylene Rubber, Gum Compound (discontinued **)&
Copyright © lookpolymers.com All Rights Reserved