Sharadaa Ceramics Sharada RFC-80 Gel Bonded Castables

Category	Ceramic , Oxide , Aluminum Oxide
Manufacturer	Sharadaa Ceramics
Trade Name	Sharada
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Sharadaa Ceramics Sharada RFC-80 Gel Bonded Castables.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Mullite Bonded Free Flowing Cement Free Versatile Castable SystemProduct Characteristics: High Mullitisation, Free from Low Temperature eutectics, Non wetting to molten metals Ferrous/Non Ferrous, Extreme resistance to thermal, Ultra high creep resistance-High HMOR, Intricate shaped Precast blocks superior to fired and Resistance to Mill scale /AccretionIndustry Focus: Steel: Blast Furnace Trough, Torpedo Ladles, Lances/Snorkel, Burner Blocks, Reheat furnace roof/Hearth, Coke Oven door/Roof Repair, Sponge Iron DRI Maintenance, Tundish Flow control device/Well blocks/Nozzles; Cement: Burner Pipe; Non Ferrous: Non wetting to Aluminum/Copper, Lined in Melting furnace walls, Launders, Aluminum Transfer Ladles; Ceramic: Fused silica kiln furniture for Ultra Low thermal, Expansion and High resistance to thermal shock; Ferrous Foundry: Ladles; Glass: Repair of Silica Roof, Sub paving.Information provided by Sharadaa Ceramics Pvt. Ltd.

Physical Properties	Metric	English
Bulk Density	2.60 g/cc @Temperature 1400 Â°C	0.0939 lb/inÂ³ @Temperature 2550 Â°F
	2.70 g/cc @Temperature 800 Â°C	0.0975 lb/inÂ³ @Temperature 1470 Â°F
	2.80 g/cc @Temperature 200 Â°C	0.101 lb/inÂ³ @Temperature 392 Â°F
Porosity	15 %	15 %
	16 %	16 %

Mechanical Properties	Metric	English	Comments
Modulus of Rupture	0.120 GPa @Temperature 1400 Â°C	17.4 ksi @Temperature 2550 Â°F	Hot
Compressive Strength	49.0 MPa @Temperature 800 Â°C	7110 psi @Temperature 1470 Â°F	Cold Crushing
	68.6 MPa @Temperature 1400 Â°C	9960 psi @Temperature 2550 Â°F	Cold Crushing

Component Elements Properties	Metric	English	Comments
Al2O3	80 %	80 %
Fe2O3	1.5 %	1.5 %

Descriptive Properties	Value	Comments
Base Material	Low Iron Bauxite
Permanent Linear Change	-1.0 - 1.0%	1400Â°C