BASF Ultramid® B3S BK00464 PA6 (Conditioned)

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced
Manufacturer	BASF
Trade Name	Ultramid®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	BASF Ultramid® B3S BK00464 PA6 (Conditioned).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: Easy flowing, finely crystalline injection-molding grade for very fast processing. Uses include thin-walled technical parts (eg. housings, fittings, grips, small parts and fixing clamps).Information provided by BASF

Physical Properties	Metric	English	Comments
Density	1.13 g/cc	0.0408 lb/in³	ISO 1183
Water Absorption	9.0 - 10 %	9.0 - 10 %	Saturation; ISO 62
Moisture Absorption at Equilibrium	2.6 - 3.4 %	2.6 - 3.4 %	23°C; 50% RH; ISO 62
Viscosity Measurement	145	145	ISO 307
Linear Mold Shrinkage	0.0055 cm/cm	0.0055 in/in	restricted
Melt Flow	197.75 g/10 min @Load 5.00 kg, Temperature 275 °C	197.75 g/10 min @Load 11.0 lb, Temperature 527 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	45.0 MPa	6530 psi	50 mm/min; ISO 527-1/-2
Elongation at Yield	20 %	20 %	50 mm/min; ISO 527-1/-2
Modulus of Elasticity	1.20 GPa	174 ksi	ISO 527-1/-2
Izod Impact, Notched (ISO)	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F	ISO 180/A
Charpy Impact Unnotched	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F	ISO 179/1eU
Charpy Impact, Notched	5.00 J/cm² @Temperature 23.0 °C	23.8 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eA
Tensile Creep Modulus, 1000 hours	1100 MPa @Strain <=0.500 %	160000 psi @Strain <=0.500 %	ISO 899-1

Thermal Properties	Metric	English	Comments
Specific Heat Capacity	1.70 J/g-°C	0.406 BTU/lb-°F
Thermal Conductivity	0.330 W/m-K	2.29 BTU-in/hr-ft²-°F	DIN 52612
Melting Point	220 °C	428 °F	DIN 53765
Maximum Service Temperature, Air	87.0 °C	189 °F	for 50% loss of tensile strength after 20000hr
	97.0 °C	207 °F	for 50% loss of tensile strength after 5000hr
	180 °C	356 °F

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+10 ohm-cm	1.00e+10 ohm-cm	IEC 60093
Surface Resistance	1.00e+10 ohm	1.00e+10 ohm	IEC 60093
Dielectric Constant	7.0 @Frequency 1.00 Hz	7.0 @Frequency 1.00 Hz	IEC 60250
Dissipation Factor	0.30 @Frequency 1.00e+6 Hz	0.30 @Frequency 1.00e+6 Hz	IEC 60250
Comparative Tracking Index	600 V	600 V	Test solution A; IEC 60112

Processing Properties	Metric	English	Comments
Melt Temperature	250 - 270 °C	482 - 518 °F	Injection-molding/Extrusion
Mold Temperature	40.0 - 60.0 °C	104 - 140 °F	Injection-molding

Descriptive Properties	Value	Comments
Commercial Status	Europe