BASF Ultramid® B3GM35 BKQ649 23220 15/25% Glass/Mineral Filled PA6 (Dry)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass/Mineral Reinforced |
| Manufacturer | BASF |
| Trade Name | Ultramid® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultramid® B3GM35 BKQ649 23220 15/25% Glass/Mineral Filled PA6 (Dry).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Ultramid B3GM35 BKQ649 23220 is a 40% combined glass-fiber and mineral reinforced, pigmented black injection molding PA6 grade.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.48 g/cc | 0.0535 lb/in³ | ISO 1183 |
| Water Absorption | 6.6 % | 6.6 % | ISO 62 |
| Moisture Absorption at Equilibrium | 2.0 % | 2.0 % | 23°C/50% R.H.; ISO 62 |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | ASTM Data; MD |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 122 MPa | 17700 psi | 5mm/min; ISO 527 |
| Elongation at Break | 3.8 % | 3.8 % | 5mm/min; ISO 527 |
| Flexural Modulus | 7.80 GPa | 1130 ksi | ISO Data |
| Izod Impact, Notched (ISO) | 3.80 kJ/m² | 1.81 ft-lb/in² | ISO Test |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | 10 K/min |
| Deflection Temperature at 1.8 MPa (264 psi) | 198 °C | 388 °F | ISO 75 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | BK23220 | |
| Commercial Status | Active America | |
| Impact Modified | No | |
| Primary Processing Technique | Injection Molding |
Users viewing this material also viewed the following:
- Kingfa FRHIPS-301 Flame Retardant Polystyrene
- LG Chemical KEYFLEX BT 1045D Ester Type TPE
- H.C. Starck Amperweld® 1701.39 K4 Chromium Carbide RIII
- Lushan PA6+30% GF Nylon Toughener/PA Impact Modifier
- SABIC Innovative Plastics LNP Thermocomp YF004 Polyester Elastomer
- Lubrizol STAT-RITE® X-5091 Ether-Type Static Dissipative Polymer
- Master Bond EP37-3FLF Low Exotherm Highly Flexible Two Component Epoxy
- Arlon CP-414R Silicone Rubber
Copyright © lookpolymers.com All Rights Reserved