BASF Ultramid® A34 01 PA66 (Conditioned)

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced, Flame Retardant
Manufacturer BASF
Trade Name Ultramid®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® A34 01 PA66 (Conditioned).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ultramid A34 01 is an intermediate visosity, PA66 grade. It conforms to FDA requirements including, 21 CFR 177.1500,EU Directive 2002/72/EC, the German BfR recommendation "X Polyamide", 1.6.1998 or legislations for other countries will be provided on request.
Physical Properties Metric English Comments
Density 1.13 g/cc
0.0408 lb/in³
dry; ISO 1183
Water Absorption 8.5 %
8.5 %
beginning dry; ISO 62
Moisture Absorption at Equilibrium 2.2 %
2.2 %
beginning dry (23°C/50% R.H.); ISO 62
Relative Viscosity 3.5 cP
3.5 cP
ISO Test; 96 % SAV
Viscosity Test 205 cm³/g
205 cm³/g
Viscosity number
Linear Mold Shrinkage 0.014 cm/cm
0.014 in/in
ASTM Data; MD
Melt Flow 40 g/10 min

@Load 5.00 kg,
Temperature 275 °C
40 g/10 min

@Load 11.0 lb,
Temperature 527 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 60.0 MPa
8700 psi
50mm/min; ISO 527
Elongation at Break >= 50 %
>= 50 %
50mm/min, Nominal strain; ISO 527
Elongation at Yield 20 %
20 %
50mm/min; ISO 527
Tensile Modulus 1.60 GPa
232 ksi
1mm/min; ISO 527
Charpy Impact Unnotched NB
NB
ISO 179
Tensile Creep Modulus, 1 hour 1100 MPa
160000 psi
ISO 899
Tensile Creep Modulus, 1000 hours 700 MPa
102000 psi
ISO 899
Thermal Properties Metric English Comments
Melting Point 255 °C
491 °F
10 K/min
260 °C
500 °F
ASTM Test
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+10 ohm-cm
1.00e+10 ohm-cm
IEC 60093
Surface Resistance 1.00e+10 ohm
1.00e+10 ohm
IEC 60093
Dielectric Constant 5.0

@Frequency 1.00e+6 Hz
5.0

@Frequency 1.00e+6 Hz
IEC 60250
Dissipation Factor 0.20

@Frequency 1.00e+6 Hz
0.20

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 600 V
600 V
IEC 60112
Descriptive Properties Value Comments
Color Natural
Commercial Status North America and Europe
FDA 21 CFR 177.1500
Form Pellets
Impact Modified No
Primary Processing Technique Film Extrusion
Processing Injection Molding
Other Extrusion