BASF Ultramid® 7523-2AM BK ND3007 33% Glass Filled PA66 (Conditioned)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | BASF |
| Trade Name | Ultramid® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultramid® 7523-2AM BK ND3007 33% Glass Filled PA66 (Conditioned).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Ultramid 7523-2AM BK ND3007 is an impact modified, 33% glass reinforced, heat stabilized injection molding PA6/6.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.33 g/cc | 0.0480 lb/in³ | dry; ISO 1183 |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | ASTM Data; MD |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 132 MPa | 19100 psi | 5mm/min; ISO 527 |
| Elongation at Break | 5.0 % | 5.0 % | 5mm/min; ISO 527 |
| Tensile Modulus | 8.25 GPa | 1200 ksi | 1mm/min; ISO 527 |
| Flexural Modulus | 6.85 GPa | 994 ksi | ISO Data |
| Charpy Impact Unnotched | 9.40 J/cm² | 44.7 ft-lb/in² | ISO 179 |
| 9.10 J/cm² @Temperature -30.0 °C |
43.3 ft-lb/in² @Temperature -22.0 °F |
ISO 179 | |
| Charpy Impact, Notched | 2.40 J/cm² | 11.4 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 257 °C | 495 °F | 10 K/min |
| 257 °C | 495 °F | ASTM Test |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Black | |
| Commercial Status | Active America | |
| Impact Modified | Yes | |
| Primary Processing Technique | Injection Molding |
Users viewing this material also viewed the following:
- Raschig Group DECAL® 937 Phenolic
- Overview of materials for Nylon 66, 50% Glass Fiber Filled
- LATI Latilub 87/24UV-20T PC, PTFE Filled
- SABIC Innovative Plastics LNP LUBRICOMP RI001 PA 66
- Chase Plastics CP Pryme® AC100 Acetal Copolymer
- Westlake Epolene® C-13 Coating Grade - Highly Branched Medium Molecular Weight Polyethylene Polymer
- Ascend Performance Materials Vydyne® M344 BLK Nylon 66, Flame Retardant, DAM
- BCC Products MB 1100 Polyurethane Foam Modeling Board
- A. Schulman SCHULAMID® 6 MV14 Unreinforced Nylon 6
- A. Schulman SCHULAMID® 66 GF30H 30% Glass Fiber Reinforced, Heat Stabilized Nylon 66
Copyright © lookpolymers.com All Rights Reserved