BASF Ultradur® B 4300 G3 High Speed 15% Glass Filled PBT

Category	Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer	BASF
Trade Name	Ultradur®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	BASF Ultradur® B 4300 G3 High Speed 15% Glass Filled PBT.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Description: Is a PBT, easy-flowing injection-molding grades with 15% glass fibers; for rigid, tough and dimensionally stable technical parts.Applications: Housings, consoles, contact carriers, covers.Information provided by BASF

Physical Properties	Metric	English	Comments
Density	1.41 g/cc	0.0509 lb/in³	ISO 1183
Water Absorption	0.40 %	0.40 %	Saturation; DIN 53495/1L
Moisture Absorption at Equilibrium	0.20 %	0.20 %	23°C; 50% RH
Viscosity Measurement	98	98	[ml/g]; Viscosity number; ISO 1628
Linear Mold Shrinkage, Flow	0.0063 cm/cm	0.0063 in/in	60x60x2 mm; ISO 294
Linear Mold Shrinkage, Transverse	0.011 cm/cm	0.011 in/in	60x60x2 mm; ISO 294
Melt Flow	33.84 g/10 min @Load 2.16 kg, Temperature 250 °C	33.84 g/10 min @Load 4.76 lb, Temperature 482 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	100 MPa	14500 psi	50 mm/min; ISO 527-2
Elongation at Yield	3.4 %	3.4 %	50 mm/min; ISO 527-2
Modulus of Elasticity	5.60 GPa	812 ksi	ISO 527-2
Charpy Impact Unnotched	2.70 J/cm²	12.8 ft-lb/in²	ISO 179/1eU
Charpy Impact, Notched	0.450 J/cm²	2.14 ft-lb/in²	ISO 179/1eA

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	8.00 - 9.00 µm/m-°C @Temperature 23.0 - 80.0 °C	4.44 - 5.00 µin/in-°F @Temperature 73.4 - 176 °F	DIN 53752
Melting Point	220 - 225 °C	428 - 437 °F	DSC; ISO 11357-3
Maximum Service Temperature, Air	210 °C	410 °F
Deflection Temperature at 0.46 MPa (66 psi)	217 °C	423 °F	ISO 75-2
Deflection Temperature at 1.8 MPa (264 psi)	185 °C	365 °F	ISO 75-2
Flammability, UL94	HB @Thickness 0.800 mm	HB @Thickness 0.0315 in
	HB @Thickness 1.60 mm	HB @Thickness 0.0630 in

Electrical Properties	Metric	English	Comments
Comparative Tracking Index	275 V	275 V	Test solution A; IEC 112

Processing Properties	Metric	English	Comments
Processing Temperature	80.0 °C	176 °F	Hopper Throat
Zone 1	250 °C	482 °F	Feeding zone
Zone 2	255 °C	491 °F	Compression
Zone 3	260 °C	500 °F	Metering-zone
Zone 4	260 °C	500 °F	Nozzle
Melt Temperature	225 - 250 °C	437 - 482 °F	Injection-molding
Mold Temperature	60.0 - 100 °C	140 - 212 °F

Descriptive Properties	Value	Comments
Color	Natural and Black
Commercial Status	Europe
Peripheral screw speed	< 0.25 m/s