- BASF Novolen® 2900 NC Polypropylene
BASF Novolen® 2900 NC Polypropylene
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Molded |
| Manufacturer | BASF |
| Trade Name | Novolen® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Novolen® 2900 NC Polypropylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Injection molded partsData was collected by ISO methods and provided by BASF.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.910 g/cc | 0.0329 lb/in³ | |
| Water Absorption | 0.10 % | 0.10 % | |
| Moisture Absorption at Equilibrium | 0.10 % | 0.10 % | |
| Linear Mold Shrinkage, Flow | 0.013 cm/cm | 0.013 in/in | |
| Melt Flow | 14 g/10 min @Load 2.16 kg, Temperature 230 °C |
14 g/10 min @Load 4.76 lb, Temperature 446 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 12.0 MPa | 1740 psi | |
| Elongation at Break | >= 50 % | >= 50 % | |
| Elongation at Yield | 3.5 % | 3.5 % | |
| Tensile Modulus | 0.550 GPa | 79.8 ksi | |
| Charpy Impact Unnotched | NB | NB | |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
||
| Charpy Impact, Notched | 8.50 J/cm² | 40.5 ft-lb/in² | |
| 1.50 J/cm² @Temperature -30.0 °C |
7.14 ft-lb/in² @Temperature -22.0 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 150 µm/m-°C @Temperature 20.0 °C |
83.3 µin/in-°F @Temperature 68.0 °F |
|
| Melting Point | 163 °C | 325 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 59.0 °C | 138 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 46.0 °C | 115 °F | |
| Vicat Softening Point | 35.0 °C | 95.0 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | |
| Dielectric Constant | 2.3 @Frequency 1e+6 Hz |
2.3 @Frequency 1e+6 Hz |
|
| Dielectric Strength | 140 kV/mm | 3560 kV/in | |
| Dissipation Factor | 0.000070 @Frequency 100 Hz |
0.000070 @Frequency 100 Hz |
|
| 0.00020 @Frequency 1e+6 Hz |
0.00020 @Frequency 1e+6 Hz |
||
| Comparative Tracking Index | 600 V | 600 V |
Users viewing this material also viewed the following:
- Lucent Polymers GPCB-110 Polycarbonate+PBT, 10% Glass Fiber Reinforced
- Sekisui PIOCELAN LSP-20DB Moldable Polymer Foam
- Plenco 1501 Polyester, Pellet, Injection Molded
- Wellman Wellamid® MRGF30/10 42H-GY1 Nylon 6, 30% Mineral and 10% Glass Reinforced
- Toyobo E3090A Thermoplastic Polyurethane Elastomer, Extrusion Grade
- Covestro Bayfill® EA 2001 Polyurethane Energy-Absorbing Semi-Rigid Foam, Friable Grade, MDI-based 2-Component Liquid System
- Chosun Refractories B-4 Insulating Firebrick
- Axiall 2506 Rigid PVC, Extrusion
- EG72D Polyurethane-based Biomedical Elastomer
Copyright © lookpolymers.com All Rights Reserved