BASF Luranyl® KR 2404 Polyphenylene Ether + Styrene-Butadiene Blend

Category	Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether + Styrene-Butadiene Blend , Styrene-Butadiene
Manufacturer	BASF
Trade Name	Luranyl®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	BASF Luranyl® KR 2404 Polyphenylene Ether + Styrene-Butadiene Blend.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Base grade with high heat deformation resistance and a balanced combination of stiffness and toughness. Uses include: steering-wheel covers and heater controls.Data was collected by ISO methods and provided by BASF.

Physical Properties	Metric	English
Density	1.06 g/cc	0.0383 lb/in³
Water Absorption	0.30 %	0.30 %
Moisture Absorption at Equilibrium	0.10 %	0.10 %
Linear Mold Shrinkage, Flow	0.0060 cm/cm	0.0060 in/in
High Load Melt Index	65 g/10 min @Load 21.6 kg, Temperature 250 °C	65 g/10 min @Load 47.6 lb, Temperature 482 °F

Mechanical Properties	Metric	English
Tensile Strength, Yield	55.0 MPa	7980 psi
Elongation at Break	35 %	35 %
Elongation at Yield	4.0 %	4.0 %
Tensile Modulus	2.50 GPa	363 ksi
Charpy Impact Unnotched	NB	NB
	3.00 J/cm² @Temperature -30.0 °C	14.3 ft-lb/in² @Temperature -22.0 °F
Charpy Impact, Notched	2.20 J/cm²	10.5 ft-lb/in²
	2.20 J/cm² @Temperature -30.0 °C	10.5 ft-lb/in² @Temperature -22.0 °F

Thermal Properties	Metric	English
CTE, linear, Parallel to Flow	65.0 µm/m-°C @Temperature 20.0 °C	36.1 µin/in-°F @Temperature 68.0 °F
Deflection Temperature at 0.46 MPa (66 psi)	122 °C	252 °F
Deflection Temperature at 1.8 MPa (264 psi)	111 °C	232 °F
Vicat Softening Point	125 °C	257 °F
Flammability, UL94	HB @Thickness 0.810 mm	HB @Thickness 0.0319 in

Electrical Properties	Metric	English
Electrical Resistivity	>= 1.00e+15 ohm-cm	>= 1.00e+15 ohm-cm
Surface Resistance	1.00e+14 ohm	1.00e+14 ohm
Dielectric Constant	2.6 @Frequency 1e+6 Hz	2.6 @Frequency 1e+6 Hz
	2.7 @Frequency 100 Hz	2.7 @Frequency 100 Hz
Dielectric Strength	95.0 kV/mm	2410 kV/in
Dissipation Factor	0.00050 @Frequency 1e+6 Hz	0.00050 @Frequency 1e+6 Hz
Comparative Tracking Index	300 V	300 V